此试件应使用与原始试验相同的焊接参数进行焊接,并且仅对焊接金属冲击试样进行试验。
This test piece shall be welded using the identical welding parameters as the original test and only weld metal impact test specimens shall be tested.
结果表明,经过焊后热处理后焊缝出现严重的低温脆化,其冲击试样的断口为解理状形貌;
The results show that after post-weld heat treatment(PWHT), the welds of X80 steel seriously embrittle, and the fracture morphology of impact specimens is cleavage.
在透射电镜和扫描电镜上观察分析了合金析出物的特征和冲击试样的断口形貌及断裂机制。
The aging precipitant and fracture topography were observed under TEM and SEM. The mechanism of fracture of samples was analysed.
通过改变焊缝夏比冲击试样的缺口取向,研究了缺口位向对多层焊缝金属韧性及断裂过程的影响。
By changing the nolch local ion of Charpy impact test specimens studied the effect of nolch location on toughness and cracking process in multi-layer welds.
冲击试样取样位置对焊缝冲击性能有明显的影响,板厚1/2位置的低温冲击功均低于1/4位置。
The effects of sampling position on low temperature impact property of the welds are obvious, and the impact energy of 1/2 plate thickness is lower than that of 1/4 plate.
结果表明:X70管线钢焊接接头热影响区冲击试样的冲击功与断口剪切面积基本成线性比例关系,冲击功越高,剪切面积越大。
The results indicated that impact absorbed energy of heat-affected zone in welded joint of X70 pipeline steel were proportional with shearing area on the whole.
冲击吸收功:规定形状和尺寸的试样在冲击试验力一次作用下折断时所吸收的功。单位为J。
Impact absorption work: the shape and size of the specimen in the impact test force under a role in the absorption of the power. Unit for J.
对夏比摆锤式冲击试验,一组三个试样的试验结果不符合要求,仅一个较低值低于70%,应取三个试样进行附加试验。
For Charpy impacts tests, where the results from a set of three specimens do not comply with the requirements, with only one lower value below 70 %, three additional specimens shall be taken.
艾氏冲击试验:用规定高度的摆锤对处于悬臂梁状态的缺口试样进行一次性打击,测量试样折断时冲击吸收功的试验。
The impact test of the pendulum is used to strike the notched specimens of the cantilever beam with a prescribed height, and the test of impact absorbing power when the specimen is broken.
夏比(V型缺口)冲击试验:用规定高度的摆锤对处于简支梁状态的V型缺口试样进行一次性打击,测量试样折断时冲击吸收功的试验。
Charpy impact test (V gap) : the specified height of pendulum of the one-time blow to V notched specimens in beam state, test specimen is broken by the impact absorbing energy.
该技术采用微合金化,利用正交试验设计方法,对不同成分搭配的试样进行宏观硬度和冲击韧性测试,优化了合金成分。
The composition was optimized by tiny alloying, orthogonal test design and the hardness and impact toughness test for the different samples with different combination of alloy composition.
黄麻纤维掺入聚丙烯导致黄麻纤维增强聚丙烯试样的冲击韧性摘要与断裂韧性下降。
The impact toughness and fracture toughness of the composite samples decrease after adding jute fibers when compared to pure polypropylene.
阐述了试样尺寸,温度、湿度、缺口以及缺口加工方式等因素对塑料冲击强度测试结果的影响。
It expatiated the effects of the factors, such as sample size, temperature, humidity, notch and etc, on the result of the plastic impact strength test.
用等离子喷涂方法在合金圆柱体上制备了热障涂层,并用水冷的方法进行了热冲击实验,试样的失效现象为轴向的开裂和剥落。
The plasma spraying technique was used to prepare a set of thermal barrier coating specimens, and water-cooling method was used in thermal shock experiments.
比较两种材料试样在一定时间内的失重变化情况,表明低碳高合金钢的抗冲击腐蚀磨损性能优于高锰钢。
Wear loss of specimens for these two steels during a certain time show that low carbon high alloy steel is much more resistant to corrosive impact abrasion than high manganese steel.
室温下测量了试样的拉伸和冲击性能。
The tensile and impact properties of the specimens were measured at room temperature.
介绍了一种自行设计的夏比冲击试验V形缺口试样送样卡具。
This article introduced a kind of self-designed V shape sample clamp for Sharpy impact test machine.
根据多冲载荷下激光涂层应力波的传播过程研究了涂层全覆盖基体试样在受冲击载荷下的变形情况。
The transformation of basal body with laser melted clad coating was studied according to the transmission of elastic stress wave which on a laser coating under repeated impact load.
经C路径的二次ECAE加工后试样为各向同性材料,其缺口冲击强度较PP有所提高,拉伸强度下降,断裂伸长率提高,表现出很好的延伸性。
The specimen by route C ECAE processing was isotropic and its impact strength increased, tensile strength decreased, elongation at break improved and show…
研究了TA5钛合金板材试样各种室温冲击韧性及其相互关系以及轧制工艺的影响。
Various impact toughnesses of TA5 titanium alloy plate at ambient temperature, their relationships each other and the effects of rolling process factors on the relationships are studied.
结果表明,美式落锤冲击试验受很多因素(如温度、试样尺寸和试样的成型工艺)影响。
The results showed that many factors influenced the American drop weight impact test, such as temperature, sample size and the moulding process of samples.
由热处理后试样冲击断面的SEM照片可见水分挥发留下的空洞,这些空洞容易形成应力集中点,因而导致冲击韧性降低。
Many round voids which result in stress concentration easily are found on SEM micrographs of fracture surface after heat-treatment, so the notched izod impact strength of the sample decreases.
实验发现,高应力冲击磨损后,磨损试样表层形成高硬度的白层与变形层。
The experimental results show that the high hardness white layer and plastically deformed zone are developed on the surface layer under high stress impact wear.
结果表明,采用水基工作液电火花加工,电火花加工后高温回火处理及喷丸强化等措施,都可提高试样的冲击疲劳寿命。
The results show that the impact fatigue life-time of the specimen will increase by means of high-temperature temper and shot-peening after EDM with the water-base working fluid.
本研究进行了渗硼试样的拉伸、多次冲击以及旋转弯曲疲劳试验,并与未渗硼试样进行比较。
In the present study, tensile and repeated impact as well as rotated-bending fatigue tests were carried out.
冷却速度快,试样产生的热应力大,导致冲击韧性及冷弯性能降低。
The higher the cooling rates, the greater the thermal stress, and the lower the toughness and the cold bending property of test sample.
结果表明:在强激光冲击下,试样发生显著的塑性变形,变形后轴截面形状为类圆锥形;
The specimen irradiated by intense laser generates distinct plastic deformation, and the profile of axial cross section of specimen after shocking is similar to a coniform figure.
光纤槽道能承受规定条件下的老化、冲击试验。试验后,试样不产生裂纹或脆断;
After the stated conditions of aging, impact test, the sample doesn't crack or brittle fracture.
试样经冲击后(每个试样只准冲击一次),如出现破坏时,应提高冷冻介质的温度,否则降低其温度,继续进行试验。
7 samples (each sample by shock after shock, only once) such as damage, should improve the freezing medium temperature, or reduce the temperature, continue to test.
试样经冲击后(每个试样只准冲击一次),如出现破坏时,应提高冷冻介质的温度,否则降低其温度,继续进行试验。
7 samples (each sample by shock after shock, only once) such as damage, should improve the freezing medium temperature, or reduce the temperature, continue to test.