制备方法包括配制离子液、用离子液溶解纤维素，以及再生纤维素膜制备的步骤。
The process for preparing comprises preparing ion liquids, dissolving cellulose with ion liquids and preparing regenerated fiber film.
采用田间掩埋、平皿培养和CO2释放试验分别测试了再生纤维素膜的生物降解性。
The biodegradability of regenerated cellulose film was tested by soil-burial test in field, culture-dish test and CO2 evolution test respectively.
再生纤维素膜(甘蔗渣浆制)表面直接用紫外光固化聚氨酯-丙烯酸酯制备出防水性复合膜。
A composite film with water-resistance was prepared by curing polyurethane-acrylate on regenerated cellulose film (from bagasse pulp) under UV-irradiation.
再生纤维素膜(甘蔗渣浆制)表面直接用紫外光固化聚氨酯-丙烯酸酯制备出防水性复合膜。
A composite film with water-resistance was prepared by curing polyurethane-acrylate on regenerated cellulose film (from bagasse pulp) under UV-irradiation.