灰铁、球铁及白铁凝固时即为平衡共晶温度。
The equilibrium eutectic temperature is calculated for solidification of gray, ductile and white iron.
结果表明:锰降低液相线温度和共晶温度,缩小凝固温度范围;
The results show that: manganese lowers liquidus and eutectic temperature, and narrows down the temperature range of solidification;
所有石墨化元素均降低介稳定共晶温度,而提高稳定共晶温度,并使两者间距扩大。
All graphitizing elements decrease the metastable eutectic temperature, increase the stable eutectic temperature and enlarge their distance.
另外,热处理温度与制备复合材料的冷却速度增大会导致复合材料热处理后新相组织的产生,这是由于冷却速度的增大导致共晶温度下降引起的。
In addition, the creation of new phase in the heat treated composites can be found with increasing in heat treated temperature and cooling rate, which I...
“共晶”是指一种元素或者化合物的组合,它可以在比任一成分单独时的凝固点更低的温度下保持液态。
"Eutectic" refers to a mix of elements or compound that remains liquid at lower temperature than either of its components does alone.
显然生产商需要知道产品的共晶点,而且需要使用仪器保证产品的温度是均一的。
Obviously, the manufacturer should know the eutectic point and have the necessary instrumentation to assure the uniformity of product temperatures.
经验证明,过冷现象容易发生至使制品温度虽已达到共晶点。
Experience proves, supercooling phenomenon is easy to occur to make products temperature has reached the eutectic point.
在升温的第一阶段(大量升华阶段),制品温度要低于其共晶点一个范围。
In the first stage (large heating sublimation stage), product temperature lower than the eutectic point of a range.
产品的冷冻温度应低于它的共晶点。
Typically, the product is frozen at a temperature well below the eutectic point.
通过正交试验对预冻时间和升华干燥时间进行了分析,测量了黄瓜的共晶点温度和干燥时间。
With the help of the orthogonal experimentation we analyse the academic number of the Pre-freezing and sublimation-drying time, measure co-crystal temperature and the drying time.
结果表明,随着锑含量的增加,灰口铁共晶转变温度降低;
The results show that the eutectic transformation temperature of gray iron decreases with the increase of antimony content.
共晶熔化开始温度随形变率的增大略有下降。
The melting point of eutectic decreases slightly with the increase of deformation rate.
根据共晶机理,好的降凝剂应满足碳数相匹配、结晶温度相匹配要求。
Based on crystallization mechanism, effective pour depressant should meet the requirements of carbon chain matching and crystallization temperature matching.
在未预热的熔覆层内,先共晶的奥氏体枝晶的生长,从界面开始逆温度梯度方向定向生长.直到熔覆层的表面。
On the non preheating cladding layer, the eutectic austenite dendrite growth is along the opposite direction of temperature gradient beginning from interface to face of cladding layer.
随着变质温度的升高,稀土对初晶硅的变质作用加强,而对共晶硅的变质作用减弱。
With the increase of modifying temperature, the modification of rare earth Pr enhances on primary silicon, fades on eutectic silicon.
提高热等静压温度能显著减少共晶含量。
The cast eutectic volume fractions are remarkably reduced with increasing HIP temperature.
提高热等静压温度能显著减少共晶含量。
The cast eutectic volume fractions are remarkably reduced with increasing HIP temperature.