熔敷金属组织主要是针状铁素体，少量的先共析铁素体。
Microstructure of the deposited metals is composed of acicular ferrite and a little proeutectoid ferrite.
熔敷金属组织主要是针状铁素体，少量的先共析铁素体。
The microstructure is composed of acicular ferrite and a little proeutectoid ferrite.
结果表明，随冷却速率的增大，先共析铁素体的晶粒尺寸减小，体积分数增大，针状铁素体增多；
The results show that with the increase of cooling rate, the grain size of proeutectoid ferrite decreases, the volume fraction of proeutectoid ferrite and acicular ferrite increases.
在较大焊接热输入条件下焊接，焊缝金属产生粗大先共析铁素体、过热区产生粗大粒状贝氏体，焊接接头低温冲击韧性因此降低。
The coarse primary ferrite appeared in weld metal, and coarse bainite appeared in heat-affected zone under larger heat input welding condition, which caused low...
高碳钢中加入的铬元素抑制先共析铁素体析出，减小珠光体片层间距，可明显提高抗拉强度，提高断面收缩率，改善线材的拉拔性能。
By cr microalloying, the fore eutectoid ferrite eduction is restrained, the distance between rows of pearlite is decreased, then the tensile strength, section shrinkage and drawing property of high...
结果表明，对于亚共析钢，在中温区变形、保温后可使先共析铁素体和珠光体组织大大细化，显著改善钢中铁素体和珠光体的分布状况；
The results show that, in hypoeutectoid steels, deformation at medium temperature may fine the structure and improve the distribution of ferrite and pearlite greatly;
结果表明，对于亚共析钢，在中温区变形、保温后可使先共析铁素体和珠光体组织大大细化，显著改善钢中铁素体和珠光体的分布状况；
The results show that, in hypoeutectoid steels, deformation at medium temperature may fine the structure and improve the distribution of ferrite and pearlite greatly;