胶接工艺中,胶接接头的设计是一重要的环节。
In the glue processing, the design of the gluing joint is prerequisite and important.
激光胶接焊接头的抗剥离力远大于胶接接头的抗剥离力。
The peel force of LWB joint is far greater than that of adhesive bonded joint.
结果表明,提高温度可以加速环氧胶接接头在水中的老化;
The results showed that the aging of epoxy bonded joint in water was accelerated by increasing temperature.
计算并对比研究了胶焊和点焊、胶焊和胶接接头中的应力。
Stresses in spot welded joints, adhesive bonded joints and weldbonded joints are calculated and studied using the computational model established.
胶粘剂分子链的降解是环氧胶接接头胶接性能降低的主要原因。
The reason for reduction of bonding performance of epoxy bonded joint was the degradation of epoxy adhesive.
环氧胶接接头在水中破坏失效的原因主要是渗入到胶接层的水分子取代了胶粘剂分子在金属表面的粘附。
The reason of the failure of epoxy bonded joint in water was that the epoxy adhesive on the metal surface was substituted for water.
曲线上第一载荷峰值略低于单纯胶接接头的断裂载荷,第二载荷峰值与单纯电阻点焊接头的强度基本一致。
The first peak load is lower slightly than the fracture load of adhesive bonded joints, and the second peak load is almost the same as the fracture load of the spot welded joints.
曲线上第一载荷峰值略低于单纯胶接接头的断裂载荷,第二载荷峰值与单纯电阻点焊接头的强度基本一致。
The first peak load is lower slightly than the fracture load of adhesive bonded joints, and the second peak load is almost the same as the fracture load of the spot we…
确定以某型号雷体为代表类型的水下兵器用金属承力件与复合材料的合理胶接接头方式,以达到理想的连接、防渗效果。
The reasonable bonding joint between load-bearing metal parts and composite for the present of a certain torpedo is decided to achieve the ideal bonding and leakproof.
在有限元方法的基础上,利用变密度法对单搭接胶接接头搭接区域的被粘物形状进行了拓扑优化,通过曲线拟合得到了较为合理的轮廓。
Based on finite element method, variable density method was employed to optimize the configuration of adherends in overlap region, and the curve fitting was applied to attain proper configuration.
主要研究了环氧胶接接头在不同温度水中的老化行为,并用扫描电镜(SEM)和傅立叶红外光谱仪(FTIR)分析了其失效的机理。
The effect of temperature on the aging performance of epoxy bonded joint in water was researched, and its failure mechanism was analyzed by SEM and FTIR.
研究单搭接接头胶缝中预留间隙对接头拉剪强度和应力分布的影响。
The effect of the recessing on the strength and stress distribution of adhesively bonded single-lap joints is discussed.
运用弹塑性有限元法结合实验研究了连续和间隙连接的单搭接接头应力分布规律,并考虑了胶瘤的影响。
The stress distribution of continuous and recessed bonding single-lap joints is discussed with use of elastoplastic finite element method (FEM) and experiment, considering the effect of fillet.
并定性地讨论了胶螺接接头的耐久性问题。
研究了在胶瘤中嵌入三角形金属楔块对单搭接接头强度和应力分布的影响,结果表明,金属楔块能显著提高接头的强度。
The influence of embedded trilateral cross-section metal bar in the fillet on the strength and stress distribution of single lap joints was discussed.
研究了在胶瘤中嵌入三角形金属楔块对单搭接接头强度和应力分布的影响,结果表明,金属楔块能显著提高接头的强度。
The influence of embedded trilateral cross-section metal bar in the fillet on the strength and stress distribution of single lap joints was discussed.