结晶温度随着粘度的降低而升高。
Crystallization temperature rised with decreasing viscosity.
得出了完全再结晶温度和开始过烧温度。
The fully recrystallization temperature and the on-set overheated temperature have also been obtained.
结果表明:铬和钼可提高钢的再结晶温度。
The results showed that the recrystallization temperature is increased by alloying chromium and molybdenum.
在工业纯铜中加入微量锂能提高其再结晶温度。
Trace lithium can improve recrystallization temperature of pure copper.
淬火组织经回火后,相变再结晶温度有所降低。
After tempering, structure inheritance reduces, the recrystallization temperature reduces.
在再结晶温度下,湮没特征表现为连续回复过程。
At the reerystall temperature, the feature of annihilation appears as continual recovery process.
研究了有晶种层的PLZT薄膜的结晶温度及介电性能。
The crystallization temperature and dielectric properties of PLZT thin films with PLT seeding layers were investigated.
结果表明,超临界CO2显著降低BAPC的结晶温度;
The results show that supercritical CO2 depresses the crystallization temperature of BAPC.
DSC研究表明辐照接枝产物的熔融温度和结晶温度均降低。
The DSC results showed both the melting temperature and crystallization temperature of the grafting products were decreased.
喷淋作用和反应历史的作用对水合物结晶温度和蓄冷量影响不大。
While the spraying and the history of gas hydrate has little effect on the formation temperature and cool storage capacity.
结果表明:优化的保护渣具有较高结晶温度、较低的粘度和熔点;
The results showed that optimized flux has higher crystallization temperature, lower viscosity and melting point.
高结晶温度的保护渣具有较强的脱玻化能力,且脱玻化温度较低;
The powder for higher crystallization temperature has stronger crystallization capability in annealing and lower devitrified temperature;
它们与钢的固相线和液相线温度的高低及结晶温度区间的大小有关。
With the steel line and the solid phase of the high and low liquidus temperature and crystallization temperature of the size of interval.
根据共晶机理,好的降凝剂应满足碳数相匹配、结晶温度相匹配要求。
Based on crystallization mechanism, effective pour depressant should meet the requirements of carbon chain matching and crystallization temperature matching.
冷结晶温度和熔融温度与共混比例、共混时间、温度等因素密切有关。
The blending composition, temperature and time have a dramatic effect on the cold crystallization temperature (Tc) increases and the melting Tmperature (t m).
采用新的数据处理方法获得了整个可结晶温度区间的结晶动力学参数。
The crystallization kinetic parameters of the whole crystallization range were obtained by a new data processing method.
由于渗碳体阻碍晶粒长大,所以随碳含量的增加,钢的再结晶温度升高。
The cementite phase in steels increases the recrystallization temperature and abstracts the grain growth.
进一步表明CTCBE在自然缓冷固化的表观体积根本上由其结晶温度决定。
It was further indicated that the apparent volume of CTCBE was decided by the crystallization temperature.
通过测量硬度和观察组织,确定了几种冷变形钢的再结晶温度及其影响因素。
The recrystallization temperature of cold deformed steels and its influencing factors have been studied by measuring hardness values and structure observation.
结果表明:纳米碳纤维可提高PP的结晶温度,但略降低其结晶速率和结晶度。
The results show that the carbon nanofiber can heighten the crystallization temperature of polypropylene and lower its crystallization rate and degree of crystallization in small extent.
PBT作为PET结晶促进剂,降低回收PET的冷结晶温度,提高热结晶温度。
As accelerator for PET, PBT could decrease the cooling crystallization temperature and increase the melt crystallization temperature of recycled PET.
影响猪油干法分提参数有:结晶温度、冷却速率、养晶时间、搅拌速率及分离方式。
Parameters effecting on dry fractionation of lard are crystallization temperature, cooling rate, crystal growing time, agitation rate, separating manner.
研究了熔融温度、熔融时间、冷却方式及结晶温度对尼龙66球晶形态和大小的影响。
The influence of melting temperature, melting time, crystallization temperature and cooling mode on form and size of nylon 66 was studied.
再结晶温度以上,材料内部缺陷损伤与修复的作用效果对塑性变形能力具有重要影响。
The effect of damage and fault healing has the great influence on the plasticity in materials over the recrystallization temperature.
从进料、结晶温度、浆料流速和停留时间等几个方面进行控制,降低了PTA中的PT酸含量。
The PT acid content in PTA was controlled from the aspects such as in-feeding, crystal temperature, slurry flow and residence time.
选择有效结晶温度范围小的铝合金、采用金属型铸型以及逐层凝固的冷却方式可以有效消除裂纹。
To prevent from heat crack, the choose of aluminum alloy with small crystal temperature range and the use of metal cast model, as well as adoption of gradual solidification style will be effective.
通过调整这种材料中两种元素的组份,可以得到具有不同结晶温度、熔点和结晶激活能的存储材料。
Te-free memory material with adjustable crystallization temperature, melting point and crystallization activation energy can be obtained by changing the ratio of the two compositions.
结果表明,增韧剂的加入使尼龙1212更容易结晶,结晶速度增大,结晶温度提高,熔融热焓降低;
Results indicate that crystallization of nylon 1212 become easy and crystalline velocity and degree increase, and the heat enthalpy decreases after the addition of the toughening agent.
通过实际生产从工艺角度分析了底注法生产窄结晶温度范围高强度黄铜时夹杂、缩孔缺陷的产生机理。
The mechanism of the inclusion and shrinkage cavity in high-strength brasses produced by bottom running method was analyzed from the point of view of production technology.
通过实际生产从工艺角度分析了底注法生产窄结晶温度范围高强度黄铜时夹杂、缩孔缺陷的产生机理。
The mechanism of the inclusion and shrinkage cavity in high-strength brasses produced by bottom running method was analyzed from the point of view of production technology.