The wear mechanism of TO-treated alloy was slightly abrasion.
改性钛合金的磨损机制为轻微的磨粒磨损。
The wear mechanism of the converter dedust fan is briefly analyzed.
简要分析了除尘风机的磨损机理。
It has been shown that fatigue spalling is the main wear mechanism, abrasive wear also exist.
结果表明,渗层磨损机制以疲劳剥落为主,兼有磨粒磨损。
The wear mechanism of composites is mainly repeating toughness deform and fatigue flaking off.
表面复合材料的磨损机理主要是反复塑性变形和疲劳剥落。
The wear mechanism map of the thixoformed AZ91D alloy was drawn according to the above analysis.
基于上述特征绘制了触变成型AZ91D镁合金的磨损机制图。
The article explores swirling abrasive water jet from angles of nozzle wear mechanism and drilling.
本论文从喷嘴磨损机理和钻孔效果两大部分对旋转磨料射流进行了探索性的研究。
The reason is that the impact wear mechanism is different for low and high Si bainitic cast steels.
这是因为硅使贝氏体铸钢在高应力冲击磨损下表现出不同的失效机制。
The abrasion wear mechanism of Mn copper-nickel alloy matrix-cast chromium carbide composite was studied.
研究了真空熔铸法制备的锰白铜基铸造碳化铬复合材料的二体磨料磨损机理。
Wear mechanism transferred from server abrasive to adhesion with the increasing of hardness of the composites.
随复合材料硬度的增加,磨损机理由严重磨粒磨损向轻微磨粒磨损转变。
Meanwhile, new ideas for researching casing wear mechanism and new methods to relieve casing wear are proposed.
并提出套管磨损机理研究的新思路和减轻套管磨损的新方法。
Microscopy showed that the worn surface of track shoe is a combined result of multiple types of wear mechanism.
微观分析指出:履带板表面的磨损是多种类型磨损机理的综合结果。
The wear mechanism of the nanotube layers involved abrasive wear, fatigue wear, adhesive wear and oxidative wear.
纳米管层的磨损机理主要为磨粒磨损、疲劳磨损、粘着磨损和氧化腐蚀磨损。
This paper analyses the wear mechanism of heating valve, approahes simple repair technology and material of heating valve.
分析了供热阀门的磨损机理,探讨了简单修复供热阀门的工艺和材料。
The wear mechanism was abrasive wear and adhesion transfer of the counter-parter when the volume content of PTFE was high.
当PTFE含量较高时,磨损机理除了磨粒磨损外还有对偶件的粘着转移。
The present paper deals with the bath for hard gold plating, the quantity controll and the wear mechanism of coatings as well.
简要论述了电子工业中接插件硬金镀层的耐磨机理,获得硬金镀层的镀液,节金代金以及镀金层的质量检测等问题。
According to wear mechanism of the locomotive tractive gears, from the Viewpoint of tribology, the process of gearing is analyzed.
根据机车牵引齿轮磨损机理,从摩擦学角度出发分析轮齿啮合过程。
Furthermore, at all impact power, the wear mechanism of the material changes distinctively with the time under the cyclic impact stress.
同时,在各个冲击功下,材料的磨损机理在冲击应力的循环作用下随时间发生明显变化。
The wear mechanism of the nano-composite coatings were mainly fatigue wear and that of the pure nickel coating was mainly adhesion wear.
纳米复合镀层的磨损机制以疲劳磨损为主,而纯镍镀层以粘着磨损为主。
According to the chain hinge wear mechanism, this paper advances the design requirements of the high speed wear testing machine of chain.
根据链条铰链磨损机理,提出对链条快速磨损试验机的设计要求。
The tool wear mechanism is studied by using a digital microscope to observe the topography of the diamond tool in RUD of advanced ceramics.
通过使用数字显微镜跟踪观察旋转超声钻削过程中金刚石工具表面形貌变化,研究了旋转超声钻削先进陶瓷过程中的工具磨损机理。
The conclusion on the wear mechanism of the composite by the debris topography analysis is coincident to that of the SEM analysis on the worn surface.
通过磨屑形貌分析和对磨损表面的观察与分析所得的关于复合材料的磨损机制的结论是一致的。
The wear surface morphologies were surveyed by scanning electron microscope (SEM) and wear mechanism was analyzed under the sand slurry wear condition.
运用扫描电镜观察了这几种材料在泥沙磨损条件下的磨损表面形貌,分析了它们的磨损机理。
The micro wear mechanism for PEN is plastic flow and broken of the fiber structure, while that for PI is crack initiation, extending and block fracture.
PEN薄带的微观磨损机理主要是纤维组织的塑性流动和拉断,而PI薄带的微观磨损机理为裂纹的萌生、扩张和块状剥落。
This paper discusses the processing principle for the varied shape steel fibers by restrained shaping shear method and the wear mechanism for shear bits.
论述了约束成形剪切法加工异形钢纤维的原理和剪刀片的磨损机理。
The wear mechanism of high vanadium high-speed steel is combined micro-cutting and fatigue wear with carbide particle breaking and peeling off under stress.
高钒高速钢干滑动磨损机理为显微切削和疲劳磨损的复合,并且有应力作用下碳化物的碎裂及脱落。
It is proved that the tool wear mechanism of turn-milling (aluminum) alloy is felt wear, and that of turn-milling stainless steel is fatigue-exfoliative wear.
研究表明,车铣铝合金的刀具磨损机理主要以刀具表层材料的黏结磨损为主,而车铣不锈钢的刀具磨损机理主要以刀具表层材料的疲劳—剥落磨损为主。
Establish the erosive wear mechanism of drilling string in air drilling and put forward that erosion wear is a substantial cause to promote drill string failure.
初步确立了空气钻井钻柱冲蚀磨损机理,提出钻屑冲蚀是促使钻具失效的一项重要原因。
Based on the experiment research and finite element analysis, the fretting wear mechanism and the influence factors on fatigue life are made clear in this paper.
在数值模拟结果与试验结果基础上,总结分析了微动疲劳损伤机理及寿命的影响因素及原因。
Based on the experiment research and finite element analysis, the fretting wear mechanism and the influence factors on fatigue life are made clear in this paper.
在数值模拟结果与试验结果基础上,总结分析了微动疲劳损伤机理及寿命的影响因素及原因。