These conclusions are then proved by Marshall stability test and CPN rutting test of asphalt mixtures.
通过沥青混合料的马歇尔稳定度试验与CPN车辙试验证实了以上结论的正确性。
Long term immersing Marshall test and frozen-thaw cycle test were used to investigate the anti-stripping performance of andesite asphalt mixture using cement and anti-stripping agent.
摘要采取长时间浸水马歇尔试验和多循环冻融劈裂试验方法，对掺加了水泥、抗剥落剂的安山岩集料沥青混凝土水稳定性能进行研究。
An asphalt mixture base with a high void volume was designed by volume design procedure, and optimum asphalt content of mixture was determined by Marshall test.
采用体积法设计高空隙率的基体沥青混合料并通过马歇尔试验确定其最佳沥青用量；
When active crumbs are incorporated into asphalt mixture, Marshall test, wheel-tracking test and low-temperature split test are performed to evaluate the properties of them.
用马歇尔试验、车辙试验和低温劈裂试验分别比较了活化胶粉与未活化胶粉改性后的沥青混合料性能变化。
Marshall test design methods of asphalt mixtures are used to design the TLA modified asphalt mixture and its base asphalt mixture respectively and their road performances are tested.
采用马歇尔试验配合比设计方法分别对TLA改性沥青混合料和基质沥青混合料进行了配合比设计并对其路用性能进行了检验。
Long term immersing Marshall test and frozen-thaw cycle test were used to investigate the anti-stripping performance of andesite asphalt mixture using cement and anti-stripping agent.
采取长时间浸水马歇尔试验和多循环冻融劈裂试验方法，对掺加了水泥、抗剥落剂的安山岩集料沥青混凝土水稳定性能进行研究。
The test results also show that apparent density, Marshall stability, resistance to rutting and skidding of samples containing waste glass are slightly lower than those without waste glass.
掺加一定比例的废玻璃对沥青混合料的设计沥青用量影响不大，但会降低沥青混合料的密度，并使沥青混合料试件的马歇尔稳定度、抗车辙能力和抗滑性略有降低；
Dividing criterion between coarse and fine aggregate was set by use of Marshall Test.
利用马歇尔击实试验确定了粗细集料的分界标准。
This paper compared the differences between the Marshall and Gyratory method while designing and preparing mixture by coarse aggregates crush value and combustion test.
并对比马歇尔成型方法与旋转压实成型方法在设计成型混合料方面的差异，通过试件击实后的粗集料的破碎率以及燃烧法评价；
This paper compared the differences between the Marshall and Gyratory method while designing and preparing mixture by coarse aggregates crush value and combustion test.
并对比马歇尔成型方法与旋转压实成型方法在设计成型混合料方面的差异，通过试件击实后的粗集料的破碎率以及燃烧法评价；