The Ni based alloy powder surfacing layer was obtained by light beam surfacing on the 45 steel and the microstructure of heat affected zone(HAZ) and the phase of the surfacing layer were studied.
采用聚焦光束热源在45钢母材上获得了镍基合金粉末堆焊层,研究了堆焊层的物相组成及母材热影响区的微观组织特征。
Result of cross section analysis showed that the second phase reduced within a range of several tens microns, and the depth of heat affected zone (HAZ) increased with the increment of pulses.
截面分析结果显示,表面几十微米范围内,第二相减少,且随电子束轰击次数的增加,热影响区范围增大。
In this paper, the brittle fracture probability of weldments and the fracture toughness of heat affected zone (HAZ) were investigated according to the principle of the weakest link theory.
从最弱链模型的物理本质出发,探讨了影响焊接热影响区脆性断裂的主要因素。
The results show that the maximum residual stress appears in heat affected zone (HAZ).
结果表明,最大焊接残余应力出现在热影响区。
The fracture occurres at heat affected zone (HAZ) of most fatigue specimens. This is due to the structure inhomogeneity and the higher hydrogen content of materials at HAZ.
疲劳试样多数断于接头的热影响区,造成这一结果的主要原因是热影响区的组织不均匀性和氢含量相对较高。
The microstructure in weld metal, heat affected zone (HAZ) doesn't change, but the grains in HAZ grow up.
焊缝金属、热影响区中的微观组织基本没有变化,但热影响区组织晶粒略有长大趋势。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低,原因是接头热影响区晶粒粗大所致。
The fracture toughness of the weld metal is lower than that of the base metal and the fracture toughness of heat-affected zone (HAZ) is intervenient between those of weld metal and base metal.
接头焊缝金属的断裂韧度显著低于母材,而热影响区断裂韧度则介于母材和焊缝金属之间。
Microstructure and mechanical properties changing rules of 2219 Al-alloy HAZ (heat-affected zone) with twin wire welding were studied using welding thermal simulation method.
采用焊接热模拟试验方法研究了2219铝合金双丝焊热影响区的微观结构和力学性能的变化规律。
The effect of welding line energy on microstructure and low temperature toughness of heat-affected zone(HAZ) of X70 pipeline steel was studied by welding thermal simulation method.
采用焊接热模拟技术、显微组织分析和冲击试验的方法,研究了焊接线能量对X70管线钢焊接热影响区组织和低温韧性的影响规律。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低,原因是接头热影响区晶粒粗大所致。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低,原因是接头热影响区晶粒粗大所致。