If the DFT is reduced to less than specified, the area shall be abraded as described above and an additional layer of coating shall be applied until sufficient thickness is achieved.
如果干膜厚度缩减到低于指定时，该区域按照之前描述的进行研磨，并应再涂敷额外的一层保护层直到达到足够厚度。
Also need the final inspection process, color galvanized steel layer thickness can be used to determine the thickness of the coating device, the method is simple.
还得需求最后的查验过程，彩钢板镀锌层厚度查验可采用涂层测厚仪，办法对比简洁。
It is an inevitable tendency to reduce the thickness of tin coating and alloy layer of tinplate.
减薄镀锡板的镀锡层和合金层的厚度成为目前镀锡板生产的趋势。
Where multiple layers of coating are required to achieve the specified thickness, each layer shall be applied at right angles to the preceding layer.
多层涂层应达到规定的厚度，每一层应与前一层成直角。
It was discussed that the effect of size-stability, thickness, roughness of coating layer, and ink absorption and printability of special paper for stamp in this paper.
文章论述了特种邮票纸的平整性，松厚度，涂层表面粗糙度，油墨吸收性与印刷适性的关系。
The effects of coating constituent, coating layer thickness, permeability and temperature on transfer behavior of polystyrene thermal degradation product through coating layer have been studied.
研究了涂料组成、涂层厚度、透气性、温度等对聚苯乙烯热解产物通过消失模涂层的传输特性的影响。
The effects of layer thickness, spectral characteristics, sample fineness, supports and operating temperature on emission features of infrared coating materials are summarized.
本文总结了涂层厚度、涂料的光谱特性、衬底、使用温度、颗粒度等因素对涂料红外辐射特性的影响。
With the increase of coating layer thickness and the decrease of permeability, the peak values and time increase.
涂层厚度增加、透气性下降，则传输曲线峰值增加，时间延长。
The relative thickness of alloy coating cake in mould is the key factor influencing thickness of alloyed layer on surface of casting.
铸型中合金膏块相对厚度是决定铸件表面合金层厚度的主要因素；
The thickness of PI layer depends upon the viscosity of PAA and the spin speed of coating;
聚酰亚胺的成膜厚度取决于聚酰胺酸（PAA）的粘度及旋涂转速；
3 selection should preferred coated thin fire retardant coatings, the selection of thickness of coating type paint, exterior to do decorative surface layer vibration protection.
3选用时宜优先选用薄涂型防火涂料，选用厚涂型涂料时，其外需做装饰面层隔护。
The results show that the stress in ceramic layer is mainly for lateral compressive one, and its maximal stress occurs in the place that is at the distance of 1/3 thickness from coating surface;
结果表明，陶瓷层内的残余应力主要表现为横向压缩应力，且最大值位于距陶瓷层表面1/3厚度处；
The results show that the stress in ceramic layer is mainly for lateral compressive one, and its maximal stress occurs in the place that is at the distance of 1/3 thickness from coating surface;
结果表明，陶瓷层内的残余应力主要表现为横向压缩应力，且最大值位于距陶瓷层表面1/3厚度处；