Grain growth exponent increases with the increasing of solid solution treatment temperature.
晶粒生长指数随固溶温度的升高而增加。
This paper deals with the low frequency damping of ZA27 alloy with solid solution treatment after natural ageing stability.
研究了固溶化处理的ZA2 7合金在自然时效稳定后的低频阻尼。
Hard anodizing film could be obtained on Al-Cu alloy surface which had been treated with solid solution treatment and natural aging.
经固溶处理和自然时效的铝铜合金可以进行硬质阳极氧化。
The influence of different solid solution treatment on the structure and corrosion resistant property of cast duplex stainless steel was investigated.
研究了不同固溶处理对双相铸造不锈钢的组织及其耐蚀性能的影响。
The temperature of solid solution treatment affected not only the degree of the second phase dissolved in the matrix alloy, but also the recovery and recrystallization processing level of the alloy.
固溶处理温度的高低不仅影响第二相在基体中的溶解程度，还影响合金的回复再结晶过程进行的程度。
The results show that the precipitated austenite crystals of welded joint after solid solution treatment are fewer, the grains are smaller. And the shape of austenite changes from strip to roundness.
结果表明：经固溶处理的焊缝和热影响区，晶内奥氏体析出变少，晶粒尺寸变小，同时奥氏体的形状由长条状变为圆状。
It is shown that the mechanical properties of annealed sample of 2224 aluminum alloy are improved by the combination of solid solution and aging treatment after ECAP, the size of grain is refined.
结果表明，退火态2224铝合金经e CAP挤压后，进行固溶和时效处理，明显提高了合金的力学性能，细化了合金的晶粒。
The microstructure and properties of chromium bronze after homogenizing treatment, solid solution and aging treatment, cool deformation and aging was studied.
研究了均匀化处理、固溶时效、冷变形时效等对铬青铜显微组织和性能的影响。
This paper discusses the solid solution, surface treatment and drawing deformation and drawing process of GH90 alloy spring steel wires.
本文探讨了GH90合金弹簧钢丝的固溶处理、表面处理以及拉拔变形量和拉拔工艺。
Rhombohedral ITO solid solution was metastable in air and it would be transformed to cubic ITO solid solution by heat-treatment.
刚玉型结构ITO固溶体在空气中处于亚稳态，并且在加热的条件下可以转变为萤石型结构ITO固溶体。
Heat treatment methods, such as solid solution and quenching, have greatly enhanced its mechanical strength, which also leave a large internal residual stress in it.
固溶、淬火等热处理手段极大地提高了其机械强度，但同时使其内部产生了较大的残余应力。
The effect of cooling regime after solid solution and aging treatment on hardness, electrical conductivity and impact toughness was investigated for Cu-Ni-Be alloy.
本文研究了固溶时效后不同冷却方法对铜镍铍合金的硬度、电导率和冲击韧性的影响。
Owing to the plastic deformation on the blade surface, recrystallization formed on the solid solution heat treatment. Before blade application, recrystallization zone existed already on its two sid…
叶片表面的再结晶在叶片使用之前就已存在，是由于固溶热处理前叶片的表面存在塑性变形，在固溶热处理过程中形成的。
Owing to the plastic deformation on the blade surface, recrystallization formed on the solid solution heat treatment. Before blade application, recrystallization zone existed already on its two sid…
叶片表面的再结晶在叶片使用之前就已存在，是由于固溶热处理前叶片的表面存在塑性变形，在固溶热处理过程中形成的。