In hot mill production the slabs have to be heated to a certain degree of temperature, so that the slabs would be more plastic and easier to be rolled.
在轧钢厂的热轧生产中，必须将要轧制的板坯加热到一定的温度，使它具有一定的可塑性，才能轧制。
In order to investigate the bending behavior of the composite slabs with closed profiled sheeting and concrete, experiments are conducted on 4 simply supported composite slabs.
为了得到闭口型压型钢板-混凝土组合板的受弯性能，进行了4块闭口型压型钢板简支组合板的试验。
In 1999, the cross cracks occurred frequently in cc slabs cast in our plant, and brought a serious influence to slabs quality.
1999年我厂板坯连铸生产中频繁出现横裂纹，严重影响铸坯质量。
This article introduced the process to improve the CC slabs quality by controlling each important parameter in CC process of the research and the development of Hull Structural ship slabs.
本文介绍了首钢在开发高强船板的过程中，通过对连铸工艺各个重要参数的控制，改进高强船板铸坯外部质量的情况。
The result suggests that the cavity beneath cement concrete pavement slabs and the vehicle overloading are the important factors in incipient fracture of cement concrete pavement slabs.
结果表明，水泥混凝土路面板下脱空、超载车辆和重载车辆是造成水泥混凝土路面板早期断裂的重要因素。
Measures are taken to decrease non - order slabs in aspects of the resource of non-order slabs, operation process and quality management. The amount of non-order slab decreased 50%.
为减少无委托板坯，从无委托板坯产生的源头、操作过程和质量管理等方面采取了措施，使无委托板坯下降50%以上。
To prevent defects of continuous cast slabs, it must be considered to control the stresses and strains in slabs in casting machine design and operation.
为防止板坯连铸中的缺陷，铸机的设计及生产必须考虑到控制铸坯上的应力和应变。
The defects on pinhole bubble formed in slabs result from badness deoxidization, and the defects on large volume bubbles formed in slabs result from the high flux of argon during casting.
铸坯内产生针孔气泡缺陷的原因是钢液脱氧不良，产生大体积气泡缺陷的原因是铸机浇注过程中氩气流量过高。
The Test result showed that shear capacity is higher for the thicker composite slabs, the smaller shear span, the more distributed reinforcing bar in the composite slabs.
试验结果表明：组合板越厚、剪跨越小、剪力横向钢筋越多，组合板纵向受剪承载力就越高。
The Test result showed that shear capacity is higher for the thicker composite slabs, the smaller shear span, the more distributed reinforcing bar in the composite slabs.
试验结果表明：组合板越厚、剪跨越小、剪力横向钢筋越多，组合板纵向受剪承载力就越高。