The results indicate that the semi-solid slurry with much finer and uniformer primary phase particles is gained by self-inoculation method.
结果表明,通过自接种法得到具有更细的单相颗粒的半固体泥浆。
Semi-solid slurry of A356 alloy is prepared by compound process, and the fractal characteristic of morphology in semi-solid primary phase is studied.
利用复合工艺制备了A356铝合金半固态浆料,研究了半固态A356铝合金初生相形貌的分形特征。
Research method and main results is as following: Using electrical resistance furnace and cooling slope to melt A356 aluminum alloy and gain the semi-solid slurry.
研究方法和主要成果如下:使用电阻炉熔炼a356铝合金,并采用斜坡冷却法进行半固态熔体的制备。
The preparation method leads the stirring force field and the temperature field of the slurry to be more uniform, thereby obtaining the high-quality semi-solid slurry.
这种制备方法将使浆料受到的搅拌力场和温度场更加均匀,从而得到优质的半固态浆料。
The A356 aluminum alloy semi-solid slurry by damper cooling tube method was prepared under different pouring temperature conditions, and was compared with ones by cooling slope method.
介绍了阻尼冷却管法制备a 356铝合金半固态浆料工艺的试验装置及其工艺流程,在不同浇注温度下进行了系列试验,并与冷却斜槽法进行了对比分析。
Semisolid metal processing technology is regarded as one of the near-net shape forming technologies with wide application in 21 century, and the preparation of semi-solid slurry is the key technique.
半固态金属加工技术被认为是21世纪最具有发展前途的近净成形技术之一,其关键环节是半固态浆料的制备。
The effect of forming temperature, injection pressure and piston velocity on the filling ability of semi-solid A356 aluminum alloy slurry were investigated.
研究了半固态A356铝合金浆料的成形温度、压射比压和压射冲头速度对半固态A356铝合金流变压铸充填性的影响。
With the rise of temperature in squeeze process, the Theological property of semi-solid magnesium alloy slurry was improved.
在半固态挤压成形过程中,随着成形温度的升高,镁合金半固态浆料的流变性改善。
The influence of shear rate of the twin-screw stirring mixer with high shear rate on the quality of semi-solid magnesium alloy slurry has been studied by rheo-diecasting process.
采用半固态流变压铸成形工艺,研究了高剪切速率双螺杆机械搅拌制浆机中剪切速率对半固态镁合金浆料质量的影响规律。
The results show that shearing rate, solid rate and cooling speed have great effects on apparent viscosity of semi-solid AZ91D slurry.
结果表明:剪切速率、固相率和冷却速度对半固态浆料的表观粘度都有很大的影响。
It is found that the prepared A356 al alloy semi-solid rheological slurry by the complex method can meet the requirements of rheological casting.
研究了浇注温度、搅拌功率和搅拌时间对A356铝合金的半固态浆料的影响。
It is found that the prepared A356 al alloy semi-solid rheological slurry by the complex method can meet the requirements of rheological casting.
研究了浇注温度、搅拌功率和搅拌时间对A356铝合金的半固态浆料的影响。