Abstract: The research of laser transformation hardening on steel 980 has been done in this paper. The width, depth and microhardness of quench zone was measured.
摘要：对980钢进行激光相变硬化研究，分别对其空冷和水冷时淬火硬化层的宽度和深度进行测量，对其组织和硬化层硬度进行分析。
One of the greatest contributors to non-uniform hardness, increased thermal stresses, cracking and distortion is non-uniform fluid flow throughout the quench zone in production quench tanks.
造成淬火后工件硬度不均匀、热应力增加、畸变和开裂，主要是因为淬火槽内整个淬火区的液流不均匀。
To quench 20 steel in critical zone under different intensity alternation magnetic field and to observe the microstructure after phase transformation.
对20钢进行不同强度交流磁场下的临界区淬火处理，观察相变后的组织。
The principal problems with respect to roll working life are cracking at the surface of roll for hot-rolling and that effective zone of quench-hardening of roll for cold-rolling is too narrow.
热轧工作辊的裂纹损坏和冷轧工作辊有效淬硬层过浅是两大突出问题。
The principal problems with respect to roll working life are cracking at the surface of roll for hot-rolling and that effective zone of quench-hardening of roll for cold-rolling is too narrow.
热轧工作辊的裂纹损坏和冷轧工作辊有效淬硬层过浅是两大突出问题。