The stress corrosion cracking(SCC)behavior of X70 steel welded joint was investigated in a near-neutral pH solution by fluctuant slow strain rate test(F-SSRT).
分析温度、应力(应变)和慢应变率等因素对极化曲线的影响,并讨论温度、应力和慢应变率对管道钢发生应力腐蚀开裂的驱动作用。