The formation process of SIMOX structure during low temperature annealing are also discussed in the paper.
本文还讨论了退火期间SIMOX结构的形成过程。
The formation of oxygen precipitates and threading dislocations in top Si layer could be avoided by low temperature annealing.
低温退火可以避免在顶部硅层中氧沉淀及延伸位错等缺陷的形成。
The affection of different annealing process conditions on TiN film stress is also researched, low temperature annealing of film can be realized.
论文还研究了不同退火工艺条件对薄膜应力的影响，可以实现薄膜低温退火。
Relatively low ordering temperature for the multilayer is due to the extra driving force of ordering process caused by the vanishing of the multilayer interface at annealing.
多层膜化促进有序化在较低的温度下进行，这是由于热处理过程中多层膜界面的消失提供了有序化过程额外的驱动力。
Thecomplete annealing temperature of the defects for low fluence irradiated GaP was250K lower than that for high fluence irradiated GaP.
而高住量辐照样品中观察到比双空位更复杂的缺陷形式，其完全被退火的温度比低剂量辐照的高250k。
There are precipitation strengthening effect during nature aging and low-temperature annealing, however, the conductivity remains stable basically.
材料在自然时效与低温退火过程中，有沉淀强化效应产生，但导电率基本保持稳定。
A novel low temperature switch material VO2 thin film was fabricated by ion-sputtering and annealing.
采用离子束溅射和退火工艺制备了一种新的相变型薄膜vo2。
The experimental results show that the ratio of the bar-like defects to the point-like ones decreases with increase in time of nucleation annealing at a low temperature.
实验结果表明，棒状缺陷和点状缺陷的数量比随低温成核退火时间的增加而减小；对于相同的成核时间，棒状缺陷和点状缺陷的比随成核温度增加开始上升，后来下降。
A method of annealing for a long time at low temperature can be used to improve the plasticity and make the products acceptable.
提出用低温长时间退火的方法改善其塑性，通过试验确定了退火工艺制度，使产品的变形性能达到了使用要求。
Hardness can do 61 — 65hrc maturation process is: annealing, softening after casting machining, machining of air cooling after quenching and low temperature stress tempering.
硬度能做到61——65hrc成熟工艺是：铸造后软化退火，便于加工，加工后空冷淬火加低温去应力回火。
Hardness can do 61 — 65hrc maturation process is: annealing, softening after casting machining, machining of air cooling after quenching and low temperature stress tempering.
硬度能做到61——65hrc成熟工艺是：铸造后软化退火，便于加工，加工后空冷淬火加低温去应力回火。