Under the action of tensile stress and tensile stress, the bolt with relatively low strength will crack first, and then the fatigue fracture will occur.
在拉应力和应拉力交替的作用下，强度相对较低的螺栓会先产生裂纹，进而发生疲劳断裂。
Longitudinal crack of drill pipe box joint is brittle fracture at low stress.
钻杆接头的各种纵向开裂属于低应力脆性断裂。
Fracture morphology is more rough in room temperature, low fatigue stress and more fatigue cycles, but the length of fiber pullout is longer.
室温及疲劳循环应力低、循环周次多的断口粗糙度大，纤维拔出较长；
To strong stress sensitivity formation, low BHP reduces pore fluid pressure of near wellbore are which results in the closure of formation fracture.
对于应力敏感性强的储集层，过低的井底压力降低了近井地带地层的孔隙流体压力，导致裂缝趋于闭合。同时，井壁失稳的可能性也大。
In this paper, through analyzing the subcritical crack growth, a new formula is presented which can be used to calculate the crack fracture initiation stress at low and middle stress rates.
本文通过裂隙亚临界扩展的分析，提出一个计算低、中等应力率下裂隙断裂起动应力的新公式。
The result shows that the fracture mode is low stress brittle fracture. The fracture is mainly caused by needle type martensite in the heat affected zone of the weld joint.
结果表明，在连接杆焊缝附近的热影响区中存在大量针状马氏体组织，在低应力的作用下，导致材料发生脆性断裂。
Temperature impacted on the fracture stress and elastic modulus of the material obviously. Elevated temperature will lead to low fracture stress and smaller elastic modulus.
温度对断裂应力和弹性模量的影响也比较明显，高温会导致低的断裂应力和小的弹性模量。
The failure of the driving shaft in a hoister is caused by typical brittle fracture under low stress.
卷扬机传动轴的断裂为典型的低应力脆断事故，主要原因是传动轴的组织疏松、晶粒粗大、。
In the material with relatively low cross-linking density, extensive fracture process stripe is formed which is induced by the combined stress field near the rubber particles.
在交联密度较低的材料中，在橡胶颗粒附近叠加的应力场诱发下发生纵深度较大的断裂过程。
The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
研究表明该钢具有较好的抗应力腐蚀性能，其应力腐蚀断裂形貌为穿晶、解理断裂，并有二次裂纹。
Objective: To research the biomechanical character of a new type low stress-shielding interlocking nail for treatment of femoral fracture.
目的：研究新型股骨低应力遮挡交锁髓内钉治疗股骨干骨折的生物力学特性。
The main reason of inclined pipe fracture was low frequency stress fatigue failure at temperature field.
斜管开裂的主要原因是温度场下的低频应力疲劳破坏。
The main reason of inclined pipe fracture was low frequency stress fatigue failure at temperature field.
斜管开裂的主要原因是温度场下的低频应力疲劳破坏。