The effect of carbon and chromium content on the impact fatigue resistance and impact abrasion resistance of pearlitic low chromium cast iron has been investigated in this paper.
研究了碳、铬含量对珠光体基体低铬铸铁冲击疲劳抗力及冲击磨损性能的影响。
The corrosion wear resistance of low chromium white cast iron increases when the silicon content increases in it.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The effects of nitrogen on the properties of low carbon high chromium cast iron were studied by mechanical property and wear resistance test, and metallograph analysis using OM and ESEM.
通过力学性能和耐磨性能测试、金相组织观察和ESEM形貌分析,研究了氮含量对低碳高铬铸铁性能的影响。
The effect of re modification and heat treatment on formation of thermal fatigue crack in low chromium wear-resistant cast iron was investigated.
研究了稀土变质及热处理对低铬耐磨铸铁热疲劳裂纹形成的影响。
The effect of Si and Cu on the corrosive wears resistance of low chromium white cast iron for making grinding body of large grinding ball mill used in mine was studied in the conditions of laboratory.
以大型矿用球磨机研磨体为应用对象,在实验室条件下研究了硅、铜对低铬白口铸铁腐蚀磨损耐磨性的影响。
The low chromium white cast iron had been treated with different cooling rates after 40% deformation .
对低铬白口铸铁经过40 %热变形后,用不同冷却方式下得到的组织与力学性能进行了研究。
Erosion wear experiments were done for low-chromium cast iron containing nickel with two different heat treatments by MCF-30 erosion test machine.
采用M CF - 30型冲蚀磨损试验机对两种不同热处理后的低铬铸铁进行冲蚀磨损实验。
The results show that the corrosion wear resistance of low chromium white cast iron decreases with the increase of Cu2 + ion concentration in slurry.
结果表明,当浆料介质中铜离子浓度增加时,低铬白口铸铁的腐蚀磨损耐磨性降低。
The effect of Si content on the corrosion wear resistance of low chromium white cast iron in the slurry with Cu2+ ion was studied by three-body corrosion wear test.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The effect of Si content on the corrosion wear resistance of low chromium white cast iron in the slurry with Cu2+ ion was studied by three-body corrosion wear test.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。