Useful reference is provided for further application of low-temperature rolling in domestic wire rod production.
为国内在棒线材生产中进一步应用低温轧制工艺提供了有益参考。
The energy-saving effects of low-temperature rolling, effect of low-temperature rolling on product quality, mill load and aspects to be noted on low-temperature rolling production are discussed.
叙述了低温轧制的节能效果、低温轧制对成品质量的影响、低温轧制对轧机负荷的影响及低温轧制在生产中应注意的问题。
The results showed that the if steel has better deep drawability, higher mechanical and texture strength and elongation if the hot rolling temperature was low with big reduction in ferrite region.
结果表明,较低的铁素体轧制温度和较高的铁素体区压下量时,IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
Utilize simulation software to analyse that carry on the possibility with rolling low temperature on the existing rolling mill.
利用模拟软件分析了在现有轧机上进行低温轧制的可能性。
Low temperature rolling technology was applied for continuous rod production line in order to reduce energy consuming.
棒材连轧生产线可采用低温轧制工艺实现节能降耗。
The result shows that production of high strength screw bars is reasonable by the control rolling and control cooling process on high-speed wire mill with the capacity of low temperature rolling.
结果表明,在具有低温轧制能力的高线轧机生产线上,采用控轧控冷工艺生产高强度钢筋是可行的。
Observations showed that the micro-structure of the steel after forging or high temperature rolling was composed of low-carbon martensite, a little part of bainite and residual austenite.
微观组织观察表明,在锻造或高温轧制状态下获得了以低碳马氏体为主,含少量贝氏体和残余奥氏体的复合组织。
The effects of processing parameters of TMCP, such as finish rolling temperature and coiling temperature on microstructure and mechanical properties of low CMn steel were studied by TMCP tests.
通过TMCP工艺实验,研究了终轧温度和卷取温度对低碳锰钢力学性能和微观组织的影响规律。
The low temperature rolling technology can save energy. And it has function to the get fine crystal.
低温轧制能够实现节能降耗,同时对细化晶粒也有一定作用。
The results show that:the sheet with low temperature finish rolling has much finer grain, more homogenous microstructure than that with high temperature finish rolling;
研究结果表明:与高温精轧相比,低温精轧有利于得到细小及均匀的冷轧退火组织;
The effects of coiling temperature and cold rolling reduction ratio on deep-drawing properties of low-carbon sheets hot-rolled by FTSR of Tangsteel were investigated in laboratory.
采用唐山钢铁股份有限公司FTSR连铸连轧生产线生产的热轧卷作为生产冷轧低碳钢板的原料,研究了不同卷取温度和冷轧压下率对冷轧薄板深冲性能的影响。
With little increase in cost of steel making, the steel with good combination of strength and plasticity and satisfied toughness at low temperature can be produced by controlled rolling and cooling.
在几乎不增加冶金成本的前提下,试制钢板具有优良的强度、塑性配合,优良的低温韧性水平。
For the environmental protection and the resource recycling, a new process of rolling mill sludge disposal by the low temperature distillation was proposed.
为解决轧钢含油污泥的环境污染问题,实现铁鳞的高附加值利用,本文提出利用低温蒸馏法处理含油铁鳞新技术。
The results showed that after rolling at high and low temperature, skin-core structures also existed in the PP/LCP composite.
结果发现,PP/LCP复合材料经过高温、室温压延后仍存在皮芯结构;
It is concluded that too high fish rolling temperature, too low cooling intensity and unsymmetrical cooling are main causes.
得出终轧温度过高、冷却强度不够及冷却不均是钢筋表面起泡的重要影响因素。
Hardening, embrittling and cracking at low temperature of bitumen can be reduced due to improved flexing so as to extend the service life of road and rolling material.
改善沥青的低温屈挠性可减轻沥青低温下的发硬,发脆,龟裂,提高公路,卷材的使用寿命。
Finish rolling temperature showed great effect on yield strength and impact toughness of low V-bearing steel, but showed no obvious effect to the high V-bearing steel.
终轧温度对低V钢的屈服强度和韧性存在显著影响,但对高V钢的组织性能影响不大。
The effects of coiling temperature and cold rolling reduction ratio on deep-drawing properties of low-carbon sheets hot-rolled by FTSR of Tangsteel were investigated in laboratory.
以低碳钢为实验原料,采用不同卷取温度和冷轧压下率进行工业实验,研究了卷取温度和冷轧压下率对深冲板组织和性能的影响。
The effects of coiling temperature and cold rolling reduction ratio on deep-drawing properties of low-carbon sheets hot-rolled by FTSR of Tangsteel were investigated in laboratory.
以低碳钢为实验原料,采用不同卷取温度和冷轧压下率进行工业实验,研究了卷取温度和冷轧压下率对深冲板组织和性能的影响。