The application and research of sound emission techniques in the fatigue fracture analysis of structuaral members on railway cars are discussed in the end of paper.
最后对声发射技术在车辆构件疲劳断裂分析中的应用研究进行了探讨。
The design mainly involves the analysis of the stress, fatigue, thermal ratchet and fracture mechanics, the analysis of flow-induced vibration of the internals and the test verification.
主要涉及的内容包含每个设备部件的应力、疲劳、热棘轮、断裂力学分析和内部构件流致振动分析以及试验验证等。
Some in-site vibrating test and metal fracture analysis have been done to reveal that the crack of the U-shaped bolts is fatigue failure and some reference for designer is put forward.
结合桥梁—人行道系统的现场振动测试和螺栓试样断口分析结果,指出既有桥上发生的U型螺栓破断属于疲劳破坏,并提出了改进意见。
The toughening mechanism of ADI was investigated by microstructure analysis and fracture characteristics of the specimens under tensile test. contact fatigue and stress fatigue.
通过奥贝球铁的单调拉伸加载、接触疲劳和应变疲劳等宏观断裂规律和微观分析,探讨其强韧化机制。
The work includes several parts as the following:Firstly, fatigue and fracture reliability theory is introduced, along with the statistics theory and its application in fatigue reliability analysis.
论文首先阐述了疲劳断裂可靠性一般理论以及应用于疲劳可靠性分析中的概率统计基础理论。
This article establish the mechanics model of pendent axis of tube style centrifugal machine, analysis and calculate the fatigue and fracture safety property of pendent axis.
在管式离心机受力分析的基础上,建立了管式离心机吊轴的力学计算模型,并对吊轴的弯扭组合下的疲劳与断裂安全性作了分析计算。
The paper studies the fatigue failure probabilistic model of the weld zone in welded joint using probabilistic fracture mechanics and reliabilitistic analysis methods.
本文采用概率断裂力学方法和可靠性分析方法,针对压力容器焊接接头的组织不均匀特点,研究了焊缝区疲劳失效概率模型。
The crack size is crucial for structure fatigue design, fracture mechanics analysis, judgment criterion of fracture and fracture control.
裂纹几何尺寸是在结构的抗疲劳设计、疲劳断裂力学分析、断裂判据和疲劳断裂控制中非常重要的依据。
Methods Retrospective analysis was done on clinical imaging data of misdiagnosed fatigue fracture from 13 cases of nonspecific occupation.
方法回顾分析13例误诊的非特种职业者疲劳骨折的临床影像学资料。
This article focuses on the analysis of asphalt mixture and asphalt pavement fatigue fracture.
本文着重对沥青混合料与沥青路面的疲劳断裂进行分析。
Semiconductor analysis with ANSYS tools often incorporates nonlinear behaviors, including package warpage, solder joint creep, fracture in through-silicon-via designs, fatigue and delimitation.
利用ANSYS工具,可以分析半导体的非线性特性,其中包括封装变形、焊接点蠕变以及过孔设计中的断裂、疲劳和层间开裂。
The relative theory and methods on the analysis of the fatigue and fracture of mechanical components by means of the finite element method are discussed.
系统阐述利用有限元法对机械结构零部件进行疲劳断裂分析的相关理论和方法。
On the basic of macro-micro analysis of fracture a new fatigue-creep interaction map called first type of interaction map was constructed.
在宏观与微观分析相结合的基础上建立了第一类断裂特征图。
Through analysis, the failure reason was confirmed as that the low cycle fatigue caused by plastic deformation occurred in the lead alloy, thus the fracture occurred.
分析其失效原因为铅合金在外力作用下,产生塑性变形引起的低周疲劳,造成断裂。
The application of electron fractography to the quantitative analysis of fatigue fracture surfaces is discussed in this paper.
本文论述应用电子显微断口分析法对疲劳断面进行定量分析。
Numerical method for crack extension analysis based on fatigue fracture process of rock materials;
工程控制爆破 ,要研究岩石的定向断裂的裂纹扩展。
An Analysis on Fatigue Fracture of Oil-Suck-Rod of Non- Quenching and Tempering Steel;
采用扫描电镜等手段分析了断裂活塞,结果表明活塞断裂的性质属于疲劳断裂。
An Analysis on Fatigue Fracture of Oil-Suck-Rod of Non- Quenching and Tempering Steel;
采用扫描电镜等手段分析了断裂活塞,结果表明活塞断裂的性质属于疲劳断裂。