The distribution of elements at the sulfidation reaction product section of a sodium salt-modified desulfurization agent was analyzed by using the energy-spectrum scanning function of SEM.
利用SEM的能谱扫描功能,对钠盐调质脱硫剂硫化反应产物断面元素分布进行了分析。
The causes of the front fog lamp shield blistering after surface treatment are studied by means of metalloscopy scanning electronic microscope and energy spectrum analysis.
运用金相显微镜、描电镜和能谱仪,研究了前雾灯遮光罩表面处理后起泡的原因。
The surface defects of silver COINS was analysed with auger electron spectroscopy (AES), Scanning electronic microscope (SEM) and energy dispersive spectrum (EDS).
采用扫描电镜、能量色散谱和俄歇电子能谱检测方法,对银币表面缺陷进行了分析。
The surface topography and composition of normal coating and spot were investigated by scanning electron microscope and energy dispersion spectrum.
采用扫描电镜结合能谱的测试方法,对热处理前后含铬绝缘涂层中正常涂层和斑点的表面形貌及成分进行了分析。
By using visual examination, scanning electronic microscope, X-ray energy spectrum and metallurgy and chemical analysis, the cause of crack occurred in bellow expansion joint was analyzed.
采用宏观检查、扫描电镜、X射线能谱、金相分析及化学分析等方法,对金属波纹膨胀节开裂的原因进行了分析。
This paper analysed the pattern and composition of residual metal in diamond fracture surface by ways of Scanning Electron Microscope (SEM) and Energy Dispersion Spectrum (EDS).
采用扫描电镜(sem)和能谱(EDS)分析方法,分析了国内六种代表性的金刚石断面上残留触媒的形态及成分。
The failure of the powder metallurgy valve seat was analyzed by optical microscopy, scanning electronic microscopy, X-ray energy spectrum and X-ray diffraction.
采用力学、物理性能测试,金相、扫描电镜、能谱和X衍射分析研究了气门座圈产品失效的主要原因。
Metallographic observation, fracture scanning and energy dispersion spectrum analysis on the fractured turbine blade were carried out.
对汽轮机断裂叶片进行了金相组织观察、断口扫描及能谱分析。
The microstructure of the brazed joint was analyzed by means of a scanning electron microscope and an energy spectrum analyzer.
用扫描电镜和能谱分析仪对钎焊接头的显微组织进行了分析。
The interface between implant and bone were observed with scanning electron microscope (SEM) and X ray energy spectrum analysis (EDAX).
对种植体骨界面作扫描电镜观察、X线能谱分析。
The surface defect on medium and heavy plate Q235B was investigated by means of the optical microscopy, scanning electron microscopy and energy spectrum analysis in this paper.
对Q 235 B中厚板表面缺陷处的显微组织、非金属夹杂物等进行了金相组织和扫描电镜观察及能谱分析。
Scanning electron microscope and energy spectrum analysis was used to observe the interface of the specimen which was selected.
对预留的样本进行扫描电镜观察及能谱分析,以判断金属与陶瓷的结合界面状态。
Using X-ray diffraction, energy spectrum analysis and scanning electron microscope, TiO2 crystallite, shape and size on ceramic surface are tested.
利用x射线衍射仪、能谱分析和电子扫描电镜对瓷砖釉面表面的二氧化钛晶型、形貌、颗粒大小进行了测试。
Using X-ray diffraction, energy spectrum analysis and scanning electron microscope, TiO2 crystallite, shape and size on ceramic surface are tested.
利用x射线衍射仪、能谱分析和电子扫描电镜对瓷砖釉面表面的二氧化钛晶型、形貌、颗粒大小进行了测试。