In order to improve the fluidity of hot dipping liquid at low temperature, avoid coating thickness, and improve the coating appearance, pure aluminum often participate in 0.01% ~ 0.02%.
为了提升在较低温度下热浸镀液的流动性，避免镀层过厚，并进步镀层外观，常常参加0.01% ~ 0.02%的纯铝。
At the same temperature, the dipping time is longer, the greater the coating thickness.
在同一温度下，浸镀时间越长，镀层越厚。
The coating is easily applied by dipping or brushing and cleans up prior to curing with warm water.
该涂层可采用浸渍法和涂刷法获得，并且坯体在涂覆涂层前，需清洁然后采用热水固化处理。
For the synthesis of MEC, the novel heterogeneous catalysts have been prepared by dipping, sol-gel and surface-coating technique.
运用浸渍法、溶胶凝胶法和表面包覆法制备了多种的备选固体催化剂。
And quick wire movement during hot-dipping and inhomogeneous coating was identified as the main cause.
结果表明，钢丝热浸镀时走速过快和镀层不均匀是导致扭转脆性断裂的主要原因。
The effects of dipping temperature and time on the properties of the coating were discussed. The composition and microstructure of the coating was analyzed using SEM, EDS and other testing methods.
分析了浸镀温度、浸镀时间等对镀层性能的影响，并采用SEM、EDS等测试手段对镀层成分和结构进行分析。
No tear or break on the coating or dipping layer of P. E. coating film is allowed.
聚乙烯薄膜覆层或浸层不得出现撕裂或破损。
No tear or break on the coating or dipping layer of P. E. coating film is allowed.
聚乙烯薄膜覆层或浸层不得出现撕裂或破损。