The effect of carbon, molybdenum and rare earths on hot cracking susceptibility of austenitic stainless steel welds was studied with continuously variable deformation rate cracking test (VDR) method.
应用变形速率连续可变式热裂纹试验方法(VDR法)研究了碳、钼和稀土元素对奥氏体不锈钢焊缝热裂敏感性的影响。
The improvement of microstructure leads to a considerable reduction of the susceptibility of hot cracking of weld metal as indicated by the transverse-varestraint test.
增加焊缝中的共晶数量并改善其分布形态，从而有助于降低焊缝金属的热裂纹敏感性。