Adoption of speeded changing could reduce the degree of carbide segregation more than 3 grades whereas repeated upsetting and drawing-out could only reduce 1-1.5 grades.
本文通过大量试验和机理的研究,高速钢锻件经过反复镦拔。只能降低炭化物偏析度1~1.5级。
The effective measures are presented bo avoid zonal segregation of carbide.
提出了避免碳化物带状偏析的有效措施。
It was found that the broach was locally overheated due to band segregation of carbide, and under-tempered. These factors caused fracture of broach as a result of high internal stress.
严重的碳化物带状偏析,使拉刀产生局部淬火过热和回火不足,造成内应力急剧增高,最终导致拉刀断裂。
This paper shows that inheritance phenomenon of coarse austenite grains are due to the boundary segregation of carbide along the prior austenite grain boundary.
研究表明,调质后粗晶奥氏体的遗传现象,是由于沿原奥氏体晶界碳化物偏聚析出的结果。
This paper shows that inheritance phenomenon of coarse austenite grains are due to the boundary segregation of carbide along the prior austenite grain boundary.
研究表明,调质后粗晶奥氏体的遗传现象,是由于沿原奥氏体晶界碳化物偏聚析出的结果。