Through-thickness cracking also can lead to fatigue or stress corrosion cracking of the base metal beneath the plating.
还会形成穿透型裂纹,造成镀层下本体金属的疲劳或应力腐蚀裂纹。
The reasons of hot cracking susceptibility are analyzed through electronic-scanning, electronic-probing and energyspectrometric methods on the patterns of fracture surface of hot crack and base metal.
利用扫描、电子探针及能谱分析技术,从母材、热裂纹断口形貌等方面分析了8090合金热裂纹敏感性高的原因。
The reasons of hot cracking susceptibility are analyzed through electronic-scanning, electronic-probing and energyspectrometric methods on the patterns of fracture surface of hot crack and base metal.
利用扫描、电子探针及能谱分析技术,从母材、热裂纹断口形貌等方面分析了8090合金热裂纹敏感性高的原因。