An accelerated corrosion test was carried out on steel reinforcing bars in mortar.
本文对砂浆中埋置钢筋的试件进行了快速锈蚀试验研究。
Usually, corrosion resistance of weathering steels is evaluated by the weight-loss method in an accelerated corrosion test.
通常利用加速腐蚀试验采用失重法表征耐候钢的耐大气腐蚀性能。
Research progress on accelerated corrosion test method which can evaluate the corrosion protecveness of the post tensioning grouts is reviewed.
综述了近期国内外在后张预应力结构灌浆材料加速腐蚀实验方面的研究进展。
Using aeronautical aluminums, the accelerated corrosion tests for Marine atmospheric corrosion were studied, and a comprehensive environmental test was proposed.
针对海洋性气候条件下航空铝合金的大气腐蚀，提出了一种综合环境加速试验方法。
The corrosion resistance of samples after passivation is studied in the experiment by humid-air accelerated corrosion test, nitric acid titrating test and the brine dipping test.
将黄铜片用上述三种溶液钝化处理后，通过湿热加速试验、硝酸点滴试验、盐水浸泡试验及电化学测试对耐腐蚀性进行了研究。
The correlativity between neutral salt spray accelerated test and atmospheric corrosion test in Shijiazhuang was studied by the mass loss determination of 45 steel, A3 steel, 20 steel and gun steel.
以45钢、A3钢、炮钢、20钢为金属试样，研究它们在中性盐雾加速试验及石家庄大气环境暴露试验中腐蚀失重与时间的变化规律。
The concentration of salt and the relative areas of the large cathode coupled with a small magnesium alloy anode have an important effect on the accelerated galvanic corrosion in salt spray test.
盐雾实验中，盐的浓度、大阴极小阳极的面积比以及阴极材料相对于镁阳极的尺寸是加速镁合金电偶腐蚀的重要因素。
The dissoluble corrosion of Guangzhou metro engineering concrete in direct current was studied by an accelerated DC dissolving test of the residue mortar and correlating it with concrete.
通过加速试验方法研究了直流电流作用下混凝土筛余砂浆的溶蚀性能，并建立了其与广州地铁工程混凝土在杂散电流下的溶蚀性能之间的关系。
The chloride ion induced steel corrosion was investigated through accelerated test under applied 3v voltage. The mentioned corrosion process was studied through Linear Polarization Method.
在3V外加电压的作用下，进行混凝土中氯离子导致的钢筋锈蚀的加速试验，通过线性极化法研究钢筋的锈蚀过程。
The chloride ion induced steel corrosion was investigated through accelerated test under applied 3v voltage. The mentioned corrosion process was studied through Linear Polarization Method.
在3V外加电压的作用下，进行混凝土中氯离子导致的钢筋锈蚀的加速试验，通过线性极化法研究钢筋的锈蚀过程。