陶瓷原位胶态成形方法是制备近净尺寸复杂陶瓷部件最具应用前景的方法,硅溶胶、铝溶胶也越来越多的应用于其中。
In-situ colloidal forming of ceramics is the most promising method in making the near-net-shape and complicated ceramics, to which silica and alumina sol have been widely applied.
用2-甲基丙烯酸和硬脂酸制得的活性硅铝氧烷溶胶对NBR硫化胶无增强作用。
It was also showed that the active aluminosiloxane sol from 2-methylacrylic acid and stearic acid had no reinforcing effect on NBR vulcanized rubber.
以正硅酸乙酯和硝酸铝为原料,采用溶胶-凝胶法制备出了超细的纳米莫来石。
Fine mullite powder was synthesized by sol-gel process with tetraethoxysilane (TEOS) and aluminium nitrate as raw material.
采用溶胶-凝胶法制备硅铝二元膜包覆稀土发光材料。
The rare-earth luminescent materials coated with Si and Al were prepared by the sol-gel route.
用2 - 甲基丙烯酸与硅酸钠、硝酸铝反应,制得硅铝氧烷溶胶。
The aluminosiloxane sol was prepared by the reaction of the mixture of 2-methylacrylic acid with sodium silicate and aluminium nitrate.
采用溶胶-凝胶法制备了透明、稳定的掺铒的铝硅酸盐玻璃溶胶;
Stable and transparent Er3+ doped aluminosilicate glass sol was prepared by the sol-gel route.
本文介绍在超声波的作用下制得的硅铝氧烷溶胶、在自制的彩色水泥中加入硅铝氧烷溶胶并对彩色水泥的耐候性、耐溶剂性、耐热老化性进行测试,效果良好。
Aluminosiloxanesol is added in colored cement made by ourselves, the weather fastness, solvent resistance and aging resistance of colored cement are tried, the result is satisfying.
本文介绍在超声波的作用下制得的硅铝氧烷溶胶、在自制的彩色水泥中加入硅铝氧烷溶胶并对彩色水泥的耐候性、耐溶剂性、耐热老化性进行测试,效果良好。
Aluminosiloxanesol is added in colored cement made by ourselves, the weather fastness, solvent resistance and aging resistance of colored cement are tried, the result is satisfying.