它适合包装钢轧辊、钢绳、钢丝或汽车零件。
It is suitable for packing steel roll, steel rope, wire or automobile spare parts.
本文从制造和使用两个方面对锻钢轧辊的质量控制进行了分析。
The manufacturing and being in use quality control of forging steel rolling mill rolls was analyzed in this paper.
着重介绍铸造高速钢轧辊的性能特点、主要制造方法和在轧钢行业中的应用。
Introduced the properties, main manufacture methods and application of casting high speed steel rolls.
建议加强碳化物控制研究和优化制造工艺,以进一步提高高速钢轧辊的性能。
In order to improve properties and meet requirements, study and control of carbides in HSS and the manufacture process of HSS roll should be emphasized.
高速钢轧辊具有很强的竞争力。离心铸造法生产高速钢轧辊是主要的工艺方法。
The centrifugal foundry method is the main process to produce the high speed steel rolls which possess high competitive power.
高速钢轧辊具有硬度高、红硬性好、耐磨性好等特点,在轧钢行业获得了广泛应用。
High speed steel roll has the characteristics of high hardness, good red hardness and excellent wear-resistance, is widely used in steel rolling industry.
应用改进后的工艺热处理高速钢轧辊,轧辊裂纹率减少90%以上,明显提高了轧辊生产合格率。
After using the heat treatment process that is improved the crack rate of high speed steel rolls drops by more than 90%, which obviously improves the percent pass of product.
利用自行开发研制的DTW- 166热磨损试验机,研究了高铬铸铁、高速钢轧辊的磨损量与工艺参数的关系。
The wear characteristics of high chromium and high speed steel rolls are investigated with the DTW-166 thermal wear testing machine developed by us.
通过扫描电镜、能谱分析仪和电子探针研究了稀土复合变质剂对离心铸造的高碳高速钢轧辊组织和力学性能的影响。
The effects of RE compound modificator on the mechanical properties and microstructure of high carbon high speed steel used for roller ring were investigated by SEM, EDS and EPMA.
为此,本文得出如下结论:v、ti在半钢轧辊中起到了析出强化的作用,可以明显改善轧辊组织性能及其综合使用性能。
So we have some conclusion that the vanadium and titanium take effect in the v-ti smil-steel roller with separate out strengthening. it can be evidence improving roller's organizing and using.
介绍了山东石横特钢集团有限公司棒材车间在小规格热轧带肋钢筋切分轧制中高速钢复合轧辊的应用情况,实践证明,高速钢轧辊可有效提高作业率及产品质量。
In this paper, the application of high speed steel compound roll in splitting rolling of small gauge hot rolled ribbed bars at bar Plant of Shandong Shiheng Special steel Group co.
介绍了珠钢热连轧轧辊的应用现状及其存在的问题。
The using status and problems of rolls for hot rolling were introduced in Zhujiang steel.
模拟得到生产良好复合轧辊、漏钢等不同的生产工艺条件。
Using the simulation can get the technique of good roll cladding, bleed-out etc.
高碳高速钢是取代普通耐磨合金制造轧辊的新材质,淬火高速钢辊套硬度高,内孔加工性能差。
High carbon high speed steel (HSS) is a new material replacing common wear resistant alloy. Quenched high speed steel roll sleeve has high hardness and poor workability.
详细研究了MC 5轧辊钢球化退火工艺。
The spheroidizing annealing process of MC5 cold roll steel has been studied in detail.
涟钢CSP工作辊发生剥落的主要原因是板坯温度不均、轧辊冷却温度不均和轧制事故。
The main reasons of CSP work roll flaking in Lianyuan Steel are the uneven slab temperature, uneven roll cooling temperature and the rolling accident.
电渣重熔(esr)钢所生产的冷轧辊能显著改善冷轧辊质量,提高轧辊使用性能。
The quality and service performance of large cold roll produced by electroslag remelting (ESR) ingot can be obviously improved.
在实际应用中,轧辊过钢量提高了1.5~1.8倍,使激光熔凝处理成为提高轧辊过钢量的一个有效途径。
In application the(rolling) capacity increases by 1.5-1.8 times, that means the laser consolidation treatment is an effective(approach) to increase the rolling capacity of the rollers.
介绍了邢台机械轧辊(集团)有限公司设计的连铸机用不锈钢矩形坯液压平剪,对该液压剪的选型、剪力计算进行了分析。
The hydraulic shear for square stainless steel billet designed by our company for caster is introduced, its type selection, structure and shear stress calculation are analyzed.
对比分析了高速钢与高铬铁轧辊在热凸度、摩擦系数、氧化膜特征、抗事故性等方面的区别;
Some differences between the rolls of high-speed steel and high-chrome iron in hot crown, friction coellieient, characteristics of oxidative film and anti-accident and so on are analyzed.
高速钢用作轧辊材料使冷、热带钢工作辊寿命得到大幅度提高。
The high speed steel (HSS) as a roll material significantly increased the service life of hot and cold strip milling work rolls.
本文主要阐述锻造半钢热轧辊的制造工艺技术。
This paper mainly describes the manufacturing technology for forged semi-steel hot mill rolls.
目前国内外普遍采用电渣钢来满足大型冷轧辊苛刻的使用要求,生产成本较高。
At present, Electroslag Remelting (ESR) steel is widely used to make large cold rolls at home and a - broad for it can meet people's severe requirements for rolls, but its production cost is high.
结果表明,感应电渣离心浇铸h 13钢毛坯制造的斜轧辊,其使用寿命不低于电渣重熔锻材制造的斜轧辊。
The application results show that the service life of slanting roller made of CIESC steel H13 blank is up to that made of ESR forged steel H13 blank.
简要分析了影响薄板叠轧生产中辊耗的因素,并从轧辊保养、弹钢夹铁、辊型曲线等方面,介绍了轧辊降耗的具体措施和取得的效果。
To exploit the high performance roll is the target that the roll researchers are searching for because the quality of rolls directly affects the output and quality of the rolling material.
结果表明,电冶钢结合金组织致密、强度高、韧性好,尤其是具有高的抗磨损性能,用其所制的钢丝轧辊成本低、使用寿命高。
The results show that this material has many advantages, such as dense microstructure, high strength, toughness and wearing resistance. The roll from this material has a low cost and long life time.
结果表明,电冶钢结合金组织致密、强度高、韧性好,尤其是具有高的抗磨损性能,用其所制的钢丝轧辊成本低、使用寿命高。
The results show that this material has many advantages, such as dense microstructure, high strength, toughness and wearing resistance. The roll from this material has a low cost and long life time.
应用推荐