分析了在横列式轧机轧制大规格热轧带肋钢筋时头部葫芦状尺寸超差的产生原因,通过改进轴承座结构,有效地解决了这一问题。
The causes of the head size over tolerance of large size hot rolled ribbed bars are analyzed. By improving the structure bearing bracket, this problem was resolved well.
本文介绍了在连轧机组上采用的钢筋经分段剪切后控制冷却的工艺及有关性能。
Having been sheared into several pieces as required, the reinforced bar produced by continuous rolling process is adopted with controlled-cooling technology. Its properties are described.
结果表明,在具有低温轧制能力的高线轧机生产线上,采用控轧控冷工艺生产高强度钢筋是可行的。
The result shows that production of high strength screw bars is reasonable by the control rolling and control cooling process on high-speed wire mill with the capacity of low temperature rolling.
结果表明,在具有低温轧制能力的高线轧机生产线上,采用控轧控冷工艺生产高强度钢筋是可行的。
The result shows that production of high strength screw bars is reasonable by the control rolling and control cooling process on high-speed wire mill with the capacity of low temperature rolling.