研究添加金属铝粉和硅粉对材料性能的影响。
The influences of metallic al powder and Si powder on material performance are discussed.
同时还探讨了添加金属铝粉、有机发泡剂偶氮酰胺、乳酸铝及有机纤维的作用机理。
The mechanism of improvement of explosion resistance with addition of aluminum powder, organic foaming a-gent azodiformamide, aluminum$…
同时还探讨了添加金属铝粉、有机发泡剂偶氮酰胺、乳酸铝及有机纤维的作用机理。
The mechanism of improvement of explosion resistance with addition of aluminum powder, organic foaming a-gent azodiformamide, aluminum lactate and organic f…
实验中,研究分别添加金属铝粉和硅粉,以及同时加入金属铝粉和硅粉对试样性能的影响。
In the experiments, material performance add metallic al powder and si powder separately and simultaneously are investigated.
对在加压氮气中金属铝粉的直接氮化和氧化铝粉的碳热还原氮化法制备氮化铝粉末进行了研究。
The preparation of aluminium nitride powder by means of direct nitridation under pressurized nitrogen atmosphere and carbothermal nitridation of alumina is studied.
闪光铝粉颜料是一种重要的金属颜料。
The flash aluminum flake pigment is an important metallic pigment.
涂层中片状铝粉基本上是层层盈加,锌粉不均匀地夹杂在铝粉中,金属粉之间通过粘结剂粘结在一起。
In coat flake form aluminium powder basically is layer upon layer overlay, zinc powder did not distribute evenly in aluminium powder, glue knoted together between metal powder.
结果表明:在纯碳化硅材料中分别加入硅、铝粉之后,由于金属的延展性,在成型过程中有利的填充了碳化硅颗粒间的空隙,使得干坯更加致密。
The results show that: the specimens with metal silicon or aluminum powder become denser because the plastic metal powder contributes to filling the space.
评估结果表明,用直流等离子体氮化金属铝的特种制粉工艺所制备的超细氮化铝粉主相量已达95%。
The results of the evaluation have shown that the main phase quantity of ultrafine AlN powder prepared by the special powder manufacture, DC plasma nitridation of metallic aluminium have reached 95%.
采用自制超细铝粉配制成铝银浆,通过实验,给出了金属漆配制,涂装工艺,并对其性能进行了常规检测,其指标基本符合车用标准。
Metallic sparking coating was successfully prepared by self-developed superfine aluminum power, and the properties were generally complied with the standard of coating for automobile.
采用自制超细铝粉配制成铝银浆,通过实验,给出了金属漆配制,涂装工艺,并对其性能进行了常规检测,其指标基本符合车用标准。
Metallic sparking coating was successfully prepared by self-developed superfine aluminum power, and the properties were generally complied with the standard of coating for automobile.