试验结果表明，表面完整性中的残余应力、组织结构与表面粗糙度这三个因素对疲劳断裂抗力是最有影响力的三个因素。
The experiments have been shown that the three factors of residual stress microstructure as well as surface roughness including in the all factors of SI have most influence on the FFR.
本文就钛合金叶片电解加工后的表面粗糙度、点蚀、烧伤及吸氢等问题进行了分析并提出了改善钛合金电解加工表面完整性的措施。
The surface roughness, pitting corrosion, burn and hydrogen uptake of ECM machined Ti-alloy blades are analyzed and the measures of improving surface integrity are introduced.
本文就钛合金叶片电解加工后的表面粗糙度、点蚀、烧伤及吸氢等问题进行了分析并提出了改善钛合金电解加工表面完整性的措施。
The surface roughness, pitting corrosion, burn and hydrogen uptake of ECM machined Ti-alloy blades are analyzed and the measures of improving surface integrity are introduced.