产品特点:低气孔率粘土砖是采用低氯莫来石为主要原料,经高压成型、高温烧结而成,主要矿物组成为莫来石相。
Properties of Products: low porosity bricks USES low mullite stones as main raw material, main mineral compositions are mullite phases after pressing sintering.
由热压和液相烧结方法制得了具有各种莫来石含量和显微结构的莫来石—堇青石复合体。
Mullite - cordierite composites with various mullite contents and microstructures were prepared by liquid phase sintering and by hot pressing.
并采用合成的钛酸铝—莫来石复相材料进行了钛酸铝—莫来石窑具的制备研究。
The preparation of the aluminum titanate-mullite kiln furniture using aluminum titanate-mullite composite was studied.
采用XRD和SEM法确定莫来石-堇青石复相材料的晶相结构及其含量。
The polycrystalline structure of mullite-cordierite polyphase material and its contents were determined by XRD and SEM, respectively.
射线衍射分析结果表明,材料的主晶相为莫来石。
The XRD result shows that the main crystalline phase of the ceramic is mullite.
探讨不同配方合成的莫来石的晶相组成、晶胞参数及带有结构缺陷的莫来石固溶体的形成机理。
The influence of different ratio of raw materials on crystalline phases and unit cell parameters were studied and the formation mechanism of mullite solid solution was discussed.
研究表明,以莫来石或高岭石为主晶相的铝硅系耐火材料是精铸球铁件的理想选择。
Study has proved that ceramic shell making by Al-Si system refractory materials with main crystal of Mollite or Kaolinite will be the ideal choice for investment casting ductile iron.
晶相组成为圆柱状刚玉、圆粒状锆石和莫来石固溶体。
The crystal phase is composed of the cylinder corundum and the circle solid solution of the zirconia and mullite.
实验证实,掺加第二相显微颗粒,能有效地钉扎位错,也提高了莫来石陶瓷的常温强度。
Experhiments confirm that the addition of micro-particles of the second phase can fix the dislocations effectively, and strengthen the mullite ceramics at room temperature.
针对前脸墙鼻部烧结锆莫来石砖侵蚀物结石中常常只看到铝硅质晶相而被误判,详细介绍了烧结锆莫来石 砖的蚀变过程及侵蚀产物的岩相分析。
In the petrographic analysis of the corrosion product of zircon mullite sintered brick only the aluminosilicious crystal phase was observed, which often leads to mistake analysis result .
瓷质玻化砖磨削表面是由莫来石、玻璃相和残留石英的塑性变形和脆性断裂形成的;
The results show that the ground surface was formed by brittle fracture and plastic deformation of the compositions of ceramic tile, including mullite, g1ass phase and residual quartz.
分析表明:在不同的液相条件下,莫来石的晶粒发育产生了三种完全不同的晶形;
The SEM images indicates three different types of mullite grains could be formed according to the content of glass and the excess Al203 content.
分析表明:在不同的液相条件下,莫来石的晶粒发育产生了三种完全不同的晶形;
The SEM images indicates three different types of mullite grains could be formed according to the content of glass and the excess Al203 content.