系统研究了碱金属、铵离子和烷基胺在磺酸型阳离子交换树脂柱上以有机酸和无机酸为淋洗液的保留行为。
Retention behavior of alkali metals, ammonium ion and alkyl amines on a sulfonic cation-exchange resin column with organic acid and inorganic acid as eluent was studied.
本实验采用环氧树脂、有机仲胺、聚酰胺和封闭异氰酸酯为主要原料,合成了固体分在70%的阳离子型环氧聚合物树脂;
An epoxy resin, an organic secondary amine, a polyamide and a blocked isocyanate are selected as main materials to synthesize polymer resin with solid content of 70%.
采用苯甲酸改性的醇酸树脂和混合醚化的三聚氰胺甲醛树脂为基料,配以适量的锤纹助剂制成高固体分低温快干型氨基锤纹漆。
The high-solid fast drying amino hammer paint is prepared with benzoic acid modified alkyd resin and etherified melamine-formaldehyde resin as binder, hammering agent and other components.
偕胺肟型螯合树脂以其特殊的官能团结构、优良的吸附性能而成为从海水中提取铀的最佳材料。
Amidoxime resin is the best uranium absorption material in the sea water due to its special structure of functional group and excellent absorption property.
本文采用001氢型强酸性阳离子交换树脂从胺化废水中回收三甲胺,回收率大于90%。
In this study trimethyl amine was reclaimed from amination wastewater by using 001 hydrogenous strong-acid ion exchange resin. The recovery ratio is more than 90%.
以磷酸二氢铵、季戊四醇、三聚氰胺及丙烯酸树脂为原料研制了一种超薄膨胀型丙烯酸树脂钢结构防火涂料。
The title super-thin fire retardant intumescent coatings for steel structure is prepared with monobasic ammonium phosphate(ADP), pentaerythritol, melamine, and acrylic resin.
中文摘要本论文是以紫外光硬化型聚胺酯树脂之改质为主要目的。
In this article, the modification of the aqueous-based polyurethane is the main target.
在己内酰胺水解聚合时加入一定量的可反应型复合胺类改性剂,合成出含有胺类改性剂的尼龙6树脂。
Reactive compound amine modifiers were introduced during the polymerization of caprolactam and the nylon 6 with amine modifiers modified was obtained.
对咪唑固化四缩水甘油胺型、 缩水甘油酯与脂环型环氧树脂的固化反应特征、动力学及其固化反应活性也进行了研究。
The total curing characteristic, apparent activation energy and co-curing reactivity of tetra-glycidyl amide, glycidyl ester and aliphatic cyclo type epoxy resins cured with IMI were also i…
大孔型比凝胶型聚乙烯胺系列树脂的吸附量高。
The adsorption rate of macroporous polyvinyl amine series resin is higher than that of gelatinous resin.
阻燃型胺类环氧树脂固化剂主要包括含磷、舍氮杂环、含硅胺类固化剂,以及舍氮磷杂环和含硅一磷胺类固化剂。
The flame retarded curing agents' mainly included phosphorus-containing, nitrogen - containing, silicon-containing, phosphorus-nitrogen and silicon-phosphorus amines curing agents.
阻燃型胺类环氧树脂固化剂主要包括含磷、舍氮杂环、含硅胺类固化剂,以及舍氮磷杂环和含硅一磷胺类固化剂。
The flame retarded curing agents' mainly included phosphorus-containing, nitrogen - containing, silicon-containing, phosphorus-nitrogen and silicon-phosphorus amines curing agents.