高温氮气脱水法是在氮气保护下,高温合成聚酯多元醇。
The high temperature nitrogen dehydration method is to synthesize the certain molecular weight polyester polyol under the protection of nitrogen at high temperature.
采用逐步升高真空度的方法合成了低粘度的聚酯多元醇。
The low viscosity polyether polyol was synthesized under raising the vaccum degree step by step .
指出控制聚酯多元醇的含水量和酸值是制备聚氨酯铸模材料的关键。
It was pointed out that controlling the trace water and acid value in the polyester polyols was the key procedure to prepare the polyurethane materials suitable for making cast mould.
合成了不饱和聚酯多元醇,进而采用化学共混法合成了室温固化的聚氨酯聚苯乙烯共混物。
The room temperature curing polyurethane-polystyrene blends were synthesized with a synthesized unsaturated polyester-polyol by chemical blending method.
探讨了聚酯多元醇、泡沫稳定剂、发泡剂及催化剂等原料对硬质聚氨酯泡沫塑料制备的影响。
The influence of some raw materials such as polyester the uniformity vesica nt foams and catalysts to the preparation of rigid polyurethanes foam is also discussed.
探讨了聚酯多元醇、泡沫稳定剂、发泡剂及催化剂等原料对硬质聚氨酯泡沫塑料制备的影响。
The influence of some raw materials such as polyester the uniformity, vesicant foams and catalysts to the preparation of rigid polyurethanes foam is also discussed.
探讨了聚酯多元醇、泡沫稳定剂、发泡剂及催化剂等原料对硬质聚氨酯泡沫塑料制备的影响。
The influence of some raw materials such as polyester the uniformity vesicant foams and catalysts to the preparation of rigid polyurethanes foam is also discussed.
探讨了聚酯多元醇、泡沫稳定剂、发泡剂及催化剂等原料对硬质聚氨酯泡沫塑料制备的影响。
The influence of some raw materials such as polyester, the uniformity, vesicant foams and catalysts to the preparation of rigid polyurethanes foam is also discussed.
将涤纶废产物用二甘醇和三元醇经酯基转移合成齐聚酯多元醇,并用其制备聚氨酯硬质泡沫塑料。
A study was conducted to synthesize oligoester alcohols from poly (ethylene terephthalate) production wastes via transesterification with diethylene glycol and tribasic alcohol.
分别采用MDI- 50、TDI- 65和TDI - 80与聚酯多元醇反应制得低硬度耐溶剂聚氨酯弹性体制品。
Polyurethane elastomers with low hardness and solvent resistance were prepared by reacting MDI-50, TDI-65 and TDI - 80 with polyester polyol respectively.
采用MDI、PAPI、HDI、IPDI等不同的异氰酸酯和聚酯多元醇、聚醚多元醇等反应,制备高固体分的聚氨酯弹性体预聚物。
A high solid elastic polyurethane prepolymer has been prepared based on MDI, PAPI, HDI, IPDI and polyester polyols and polyether polyols.
合成了一种新系列丁二酸多元醇聚酯,并用它合成出耐酮类溶剂的聚氨酯弹性体。
Several succinic acid polyester polyols were synthesized and used to prepare polyurethane elastomers having excellent solvent resistance.
油与多元醇经醇解反应,进而与聚醚或聚酯、 二羟甲基丙酸、二异氰酸酯反应制得水溶性氨酯油。
Waterborne polyurethane resin is prepared by alcoholyzing oil with polyol at first, and then reacting with polyether (polyester), dimethylol propionic acid, diisocyanate.
在催化剂、链支化剂存在下多元酸和多元醇直接熔融酯化、常压缩聚合成饱和羟基聚酯。
A saturated hydroxy polyester resin has been prepared with polycarboxylic acid and polyol at the presence of catalyst and chain transfer agent by the direct melt esterification process.
在催化剂、链支化剂存在下多元酸和多元醇直接熔融酯化、常压缩聚合成饱和羟基聚酯。
A saturated hydroxy polyester resin has been prepared with polycarboxylic acid and polyol at the presence of catalyst and chain transfer agent by the direct melt esterification process.