结果表明:T91钢在高温高压水蒸汽环境下氧化层遵循“纵向裂纹不穿透破裂剥落”机理;
The results showed that rupturing and exfoliating of the oxidation layers under the high-temperature high-pressure water vapor were induced by the non-breakthrough lengthwise cracks;
结果表明:T91钢在高温高压水蒸汽环境下氧化层遵循“纵向裂纹不穿透破裂剥落”机理;
The results showed that rupturing and exfoliating of the oxidation layers under the high-temperature high-pressure water vapor were induced by the non-breakthrough lengthwise cracks;