结果表明，银基电触头材料应选用石墨坩埚熔炼，银基钎料应选择粘土坩埚熔炼。
The results show that silver based electric materials ought to be smelted by graphite crucible, the clay crucible is suitable for smelting silver based solder.
对熔化器皿玻璃等的粘土质坩埚使用中的高温软化变形、玻璃液侵蚀、热震开裂等损毁机制进行了分析研究。
Mechanism of damage of clay pot for utensil glass melting, such as softening deformation at high temperature, corrosion by molten glass, crack by thermal shock, etc was studied.