复合涂层的磨损机制主要为硬质颗粒的脆性脱落,同时伴随着轻微的显微切削。
The wear mechanism of the coating attributes to the brittleness shedding of the hard phase particles going with a slight micro-cutting.
由此,本发明所使用的模具不会与硬质颗粒相接触,用以避免模具造成损坏。
In this way, the molds will not contact with the hard grains to avoid damage.
同时研究发现了钢丝在拉拔方向上形成的以第二相硬质颗粒为核心的梭形微孔洞。
The results also presented that there were so many shuttle-shaped micro holes in this steel wires, lugging along drawing axis and cored by the hard particles.
根据失效触点成份统计分析,影响触点可靠性的颗粒物中除了硬质颗粒外,软质颗粒物也是一个不可忽略的因素。
According to statistical analysis for components of failure electric contacts, soft particles play important roles in impacting reliability of electric contacts besides hard particles.
矫顽磁力不能作为评价金属陶瓷硬质相颗粒大小的判据。
The coercive force can't be used as a criterion to estimate the grain size in the alloys.
硬质相颗粒的脱落是干式高速车铣D60钢时金属陶瓷刀具磨损的主要原因。
The main reason of ceramic tool Wearing is coming off the hard grain during the dry cutting of steel D60.
对齿轮钢钢材锯切下料时遇到的锯切障碍现象进行了系统的分析,在锯切面的局部发现了较为密集的大颗粒硬质夹杂物。
A systematic analysis of saw cutting handicap for gear steel was done, in which on local parts of saw cutting surface denser large-granular hard inclusions were found.
涂层剥落后,切削区产生的瞬时热量聚集使基体粘结相软化,从而导致硬质相颗粒脱落和基体的剧烈磨损。
After the coating broke off, the instantaneous heat builds up and softens the substrate's bonding phase, which results in breaking off of hard phase particles and sharp wear of substrate.
结果表明:名义尺寸相同而实际尺寸相差较大的磨球所磨出的粉体粒度大且分布不均匀,烧结体硬质相颗粒粗大且等轴性差,抗弯强度和硬度均较低。
It is found that the grain size of the powders milled by balls with different diameters is big, the hard phase is big too and not uniform, the hardness and bending strength are also lower.
结果表明:涂层经激光重熔处理后,WC颗粒部分分解形成W2C,同时形成新的硬质相和共晶组织。
The results show that after laser remelting, part of WC particles are decomposed into W2C, at the same time the reaction forms some new compounds.
它主要用于透明薄膜、薄片、人造革、电缆颗粒、硬质材料等。
It is mainly used for transparent film and flake, imitation leather, cable granule, rigid material, etc.
极细颗粒的硬质合金基体,使刀具的耐磨性和切削刃强度得到完美结合。
Solide carbide alioy matrix of super fine particle. Combined the abrasive resistance and cutting blade intensity of the cutting perfectly.
所述切割盘能够由烧结或胶合的金刚石颗粒或者其它的硬质材料制造。
The cutting disk can be manufactured 'from sintered or cemented diamond grit, or other hard materials.
在适当阳极氧化工艺条件下,颗粒增强铝基复合材料表面可以制得优良耐蚀性的硬质阳极氧化膜。
In a given anodic oxidation condition, a hard anodic oxidation film can be obtained on the surface of aluminum - matrix composite with an excellent anticorrosion.
在适当阳极氧化工艺条件下,颗粒增强铝基复合材料表面可以制得优良耐蚀性的硬质阳极氧化膜。
In a given anodic oxidation condition, a hard anodic oxidation film can be obtained on the surface of aluminum - matrix composite with an excellent anticorrosion.