这将会导致轧辊疲劳产生热裂、轧辊表面破裂或是疲劳层的产生。
This will lead to roll failure such as fire crack, surface crack, and fatigue failure.
制动工况不当是产生热影响层和疲劳裂纹的主要原因。
The inadepuats braking conditions are the main cause to produce heat-effected metal layer and fatigue crackings.
陶瓷涂层的热震失效是由于涂层在循环加热和冷却过程中,涂层内产生循环热应力,导致涂层发生热疲劳失效。
The thermal shock failure of ceramic coating is essentially the fatigue failure induced by cyclic thermal stress during repeated heating and cooling.
石油钻机绞车刹车鼓在下钻过程中,由于热负荷的作用会发生热疲劳破坏。
The brake rims on drilling rig drawworks are subjected to heat load during string lowering and will end in thermal fatigue failure.
受热疲劳损伤的构件表面易产生热疲劳裂纹网。
The thermal fatigue crack net is usually produced in the surfaces of components suffered thermal fatigue damage.
结果表明;我们可以利用压缩疲劳试验生热与生热—试验时间曲线来评估硫化胶的动态性能与耐热性能。
The test results show that we may estimate the dynamic and the thermal-resistant properties with the produced heat and the curve of the produced heat by the test time.
结果表明;我们可以利用压缩疲劳试验生热与生热—试验时间曲线来评估硫化胶的动态性能与耐热性能。
The test results show that we may estimate the dynamic and the thermal-resistant properties with the produced heat and the curve of the produced heat by the test time.