系统研究POSS颗粒的显微组织,钎料的熔化特性、润湿性能和力学性能。
POSS microstructure, melting characteristic, wetting property and shear strength were investigated.
本文配制了系列掺锌铌酸锂多晶料,测量了掺锌铌酸锂的熔化温度及居里温度随掺锌量的变化。
This paper synthesized a series of zinc-doped lithium niobate polycrystals, and measured the melting temperature and Curie temperature of LiNbO3:Zn versus the zinc concentration.
研究了不同镓含量银钎料的熔化温度、铺展性能、钎缝力学性能以及钎料的显微组织变化规律。
Melting temperature, spreadability, microstructures of silver filler metal with different content of gallium, and the mechanical properties of brazed joints were studied respectively.
本发明的台车本体(2),用放入了由废橡胶破碎物构成的硫化橡胶体和高分子粘合料的搅拌装置,使高分子粘合剂熔化,而后进行加压成型。
In the trolley body (2), a agitating device composing scrap rubber fragmentations is adopted for vulcanized rubber body and polymer adhesion materials which is melted and is then pressure molded.
一种选择性焊接设备,包括用于熔化的焊料(5)的料室(3)、焊料喷嘴(19)和用于经过喷嘴(19)抽吸熔化的焊料(5)的泵(9)。
A selective soldering apparatus comprises a bath (3) for molten solder (5), a solder nozzle (19) and a pump (9) for pumping molten solder (5) through the nozzle (19).
实验通过选择性地对涂敷在CCL基板上的钎料进行激光加热并熔化,最后形成焊料凸点矩阵。
The experiment is conducted by selective laser heating and melting the thin solder layer and then preprinting it on CCL in order to form the matrix with solder pads.
实验通过选择性地对涂敷在CCL基板上的钎料进行激光加热并熔化,最后形成焊料凸点矩阵。
The experiment is conducted by selective laser heating and melting the thin solder layer and then preprinting it on CCL in order to form the matrix with solder pads.