锻造钢锭多采用热锭加热，其特点是在恒温炉中一段加热和在变温炉中两段或三段加热方式。
Hot ingots are often heated in forging furnaces, the feature of which is one-stage type in a constant temperature furnace and two-or three stage type in a temperature-variable furnace.
对发生热脆锻裂的钢锭的加热规范进行了统计分析，发现现行的热锭加热规范有可能造成钢锭热脆。
After the statistical analysis of the heating specification on the hot-short ingot, we found that the heating specification of hot ingot would probably cause the ingot hot short.
以WF6和H2为原料，粉末冶金钨板为基体，采用热丝开管气流化学气相沉积试验装置，成功地制备出可变形钨锭。
Using WF6 and H2 as raw materials, tungsten plate formed by powder metallurgy as substrate, the deformable tungsten ingots were prepared successfully by a hot-wire CVD experimental facility.
以WF6和H2为原料，粉末冶金钨板为基体，采用热丝开管气流化学气相沉积试验装置，成功地制备出可变形钨锭。
Using WF6 and H2 as raw materials, tungsten plate formed by powder metallurgy as substrate, the deformable tungsten ingots were prepared successfully by a hot-wire CVD experimental facility.