最后提出了提高光学材料激光损伤阈值的方法。
At last, the suggest for improving the laser induced damage thresholds on optical materials was given.
测定了晶体的晶胞参数、折射率和激光损伤阈值。
The lattice parameters of the crystals were determined by XRD, and its lattice parameters were calculated.
还提出了提高这两种膜料的溶胶-凝胶化学膜激光损伤阈值的方法。
The method was taken out to improve the damage threshold of two kinds of materials.
实验发现，光学材料的激光损伤阈值对激光光斑大小有强烈的依赖关系。
Experimental research shows that laser induced damage thresholds (LIDT) are strongly dependent on the beam radius.
因此研究光学薄膜的激光破坏机制，如何提高激光损伤阈值，具有重要的实际意义。
Thus, it is very significant to research the damage mechanism of optical film and improve laser induced damage threshold (LIDT).
从设计和制备两方面研究提高抗激光损伤阈值的方法，并给出最终设计曲线及实测曲线。
The methods of improving the anti-damaged threshold were studied through both design and preparation. And showed the ultimate design curves and the measured curves.
文中对SiO2保护层和退火对Ta2O5薄膜的激光损伤阈值的不同影响进行了研究。
The effects of SiO2 protective layers and annealing on the laser-induced damage threshold (LIDT) of the films are investigated.
结果表明，本文制备的光纤激光器光学膜，有效的提高了激光损伤阈值，解决了低温冷镀的膜层牢固性问题。
The results indicated that the preparation of optical films of fiber laser, effectively raise the laser damage threshold, and solve the problem of the film firmly under low temperature deposition.
激光消融技术的关键在于掌握消融阈值与辐照波长的相关性，获得大的消融率和减少热损伤等等。
One of the most key problems in laser ablation is that of mastering the relativity of ablation threshold and wavelength, maximizing ablation rate, while simultaneously minimizing heat damage.
本文介绍连续CO_2激光对青紫蓝灰兔角膜损伤阈值研究的材料、方法和结果。
The material, method and results of the research on the injury threshold of rabbits' cornea caused by GW CO2 laser light are introduced in this paper.
给出了光电探测器激光能量损伤阈值的参考表达式，并对导致激光损伤的显性和隐性因素及其成因进行了分析。
The referenced expression of damage threshold fluence in laser induced detector damage is given, also the obvious and recessive damage factors and their causes are analyzed.
激光清洗存在着清洗阈值和损伤阈值。
There exist cleaning threshold and damage threshold in laser cleaning.
阐述了影响激光反射膜损伤阈值的因素以及反应磁控溅射制备高阈值激光反射膜的优势。
The factors that affect the damage threshold and the advantage of RMS in laser reflective film preparation are also discussed.
亚表面缺陷是造成固体激光器光学器件损伤阈值过低的重要原因，而表面划痕是缺陷中重要的一种。
Subsurface damage has been the main cause to lower the laser-induced damage threshold of optics components in high power solid laser system, and one important kind of these is scratch.
介绍了激光损伤的检测及损伤阈值的测量方法。
The methods of laser damage detection and laser induced damage threshold (LIDT) were introduced.
并论述不同工作参数的激光对类金刚石薄膜的激光破坏行为及其损伤阈值。
Laser induced damage mechanism and the modification of laser irradiation on the structure and characters of DLC were analysed.
通过实验，确定了激光功率、离焦量和扫描速度对清洗效果的影响，并最终确定激光清洗时的损伤阈值和清洗阈值。
The effects of the laser power, defocusing amount and the scanning velocity tO the cleaning results are got by experiments; the cleaning threshold and the damage threshold are obtained.
准确测定光学薄膜的激光损伤+阈值可以衡量光学薄膜的抗激光损伤+能力，测定损伤阈值的关键是准确地判定损伤的发生与否。
Precise measurement of the laser-induced damage threshold can be used to effectively evaluate the laser damage resistance of optical thin films.
给出了一维空间中激光热损伤的简化近似数学模型，并以此模型为基础计算了金属材料铝、银、铜的温度场分布和熔融阈值与汽化阈值。
The temperature of some metal materials and semiconductor materials have been described, and the melting damage threshold and boiling damage threshold were calculated.
由于短波长激光更易造成光学元件的损伤，因此光学元件的损伤阈值限制了氟化氪激光器的能量输出。
The damage threshold of optics limits the output of KrF laser because the laser with shorter wavelength is easier to induce damage on the optical elements.
SiO2保护层和退火都有利于提高Ta2O5薄膜的抗激光损伤能力，并且退火对提高阈值的影响更为明显。
Both SiO2 protective layers and annealing are beneficial to the damage resistance of the films and the latter is more effective to improve the LIDT.
SiO2保护层和退火都有利于提高Ta2O5薄膜的抗激光损伤能力，并且退火对提高阈值的影响更为明显。
Both SiO2 protective layers and annealing are beneficial to the damage resistance of the films and the latter is more effective to improve the LIDT.