介绍了超深冲if钢及其在汽车上应用的情况。
This paper introduces the extra-deep drawing IF steel and its application on automobiles.
介绍了深冲钢的转炉——连铸生产工艺及产品开发情况;
This paper introduces the technical process of converter continuous casting of deep drawing steel and its development of products.
为拼接超宽汽车用板,对深冲钢板进行了激光焊接试验研究。
To obtain extra wide steel sheet for automobile use experiments were conducted on laser welding of deep drawing steel sheet.
研究了锻造开坯、轧制、热处理工艺对铌带深冲性能的影响。
The niobium strips were fabricated by forging-cogging, rolling and heat treatment.
可显著提高热轧if钢的强度,但同时也导致其深冲性能降低。
P enhances the strength of hot-rolled if steel significantly, but it also reduces its deep draw ability.
介绍了采用电子背散射衍射测定深冲用再结晶铌板织构的结果。
Textures in deep punching niobium sheets have been examined by the EBSD technology in the present paper.
试验结果表明,某些汽车零件采用热轧深冲钢板生产是可行的。
Experiments' results show that it is possible using RSCA to produce some automotive parts.
同时讨论了织构形成机制,为深冲钼板的加工和研究提供了依据。
The mechanism of the textures formation were also discussed to provide a reference for the processing and research of deep drawn Mo Plates.
羟值(固体):25;柔韧,光泽,耐深冲及耐蒸煮,卷材涂料。
OH Value (Solids) : 25; Good flexibility, high gloss, Deep drawing and steam sterilization resistance, Can coating, coil coating.
介绍了本钢薄板坯连铸连轧工艺生产冷轧深冲钢(IF钢)的情况。
This paper describes the production condition of cold rolled deep drawing quality steel (IF steel) by thin slab continuous casting and rolling technique in Bengang.
羟值(固体):20;柔韧、光泽、耐深冲、卷材涂料、制罐涂料。
OH Value (Solids) : 20; Good flexibility, high gloss, Deep drawing, Can coating, coil coating.
退火状态ARCAP合金的伸长率高达45%,这使得可以深冲。
In annealed temper ARCAP alloys have an elongation up to 45% which allows deep drawing.
对唐山建龙实业有限公司SPHD深冲钢冶炼过程中的控硫技术进行了分析。
It is analyzed the controlling-sulfur technique in smelting of SPHD deep drawing steel.
应用交流阻抗技术检测,发现激光热冲击处理提高了覆镍深冲钢带的耐蚀性能。
The alternating current impedance was used to examine the corrosion resistance. It is found that laser thermal shock improved the corrosion-resistant of the deeply drawing steel strip with Ni-coating.
对连续退火或罩式退火后的深冲钢板和超深冲钢板的组织以及织构进行了观测和分析。
The structure and texture of continuous or batch annealing deep drawing and extra-deep drawing steel sheets were observed and analyzed.
本发明推荐一种用于制备可深冲或拉伸,碳含量低于0.5重量%的改良冷轧带材的工艺。
The invention relates to a process for producing improved cold-rolled band that is capable of being deep-drawn or ironed and that has a carbon content of less than 0.5 weight %.
深冲部件提供了对内部工作面镀金的能力,还可以在工作时抛光和硬化壳壁以延长产品寿命。
Deep drawn parts offer the ability to pre-plate the internal working faces with gold, while also work-polishing and hardening the wall to optimize product lifetime.
冲杯实验结果表明:复合能场铸轧板的深冲性能明显优于普通铝板,其制耳率仅为1.7%。
The drawing experimental results show that the draw ability of cast-rolled strip under composite energy field was obviously better than the general one, and the earing ratio was only 1.7%.
研究了经铁素体区热轧后的IF钢板坯在随后的一次冷轧和两次冷轧工艺中所表现出的深冲性能规律。
After being rolled in ferrite area, the IF steel was proceeded once and twice cold rolling, then its deep drawing property was studied.
AR CAP合金加工容易,无论是通过锻造,冲压,深冲,机加工,焊接或钎焊,他们也很容易镀。
ARCAP alloys are easily processed whether by Forging, Stamping, Deep drawing, Machining, Welding or Brazing and they are also easily plated.
if钢的冷轧压下率分配对深冲性能有重要的影响,是由于冷轧过程的压下率对(111)织构的形成有影响。
The reduction partition has effect important in two-time cold rolling on Drawability of IF steel, because reduction has effect in cold rolling on {111} texture.
分析了钢中各种化学元素及热轧工艺对高延伸率深冲钢板力学性能的影响 ,提出了合理的化学成分和热轧工艺制度。
The results showed that inclusion, microstructure, composition, annealing process and hot rolling process have great influence on the elongation of SPCC cold rolled plate.
通过轧制温度、轧制方式实验,以及织构和力学性能分析,研究了轧制工艺对液晶显示背光源用的深冲钼带的组织和性能的影响。
The effect of rolling process on the microstructure and mechanical properties of deep-drawing molybdenum strip was investigated in this paper through changing rolling temperature and rolling process.
以低碳钢为实验原料,采用不同卷取温度和冷轧压下率进行工业实验,研究了卷取温度和冷轧压下率对深冲板组织和性能的影响。
The effects of coiling temperature and cold rolling reduction ratio on deep-drawing properties of low-carbon sheets hot-rolled by FTSR of Tangsteel were investigated in laboratory.
结果表明,较低的铁素体轧制温度和较高的铁素体区压下量时,IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
The results showed that the if steel has better deep drawability, higher mechanical and texture strength and elongation if the hot rolling temperature was low with big reduction in ferrite region.
结果表明,较低的铁素体轧制温度和较高的铁素体区压下量时,IF钢具有更高的深冲性能、相对较高的强度、延伸率以及织构强度。
The relationship of deep-drawing property and rolling parameters of IF steel was researched by the testing of ferritic rolling and annealing.
采用作者设计的一种新型测量薄板深冲成形过程中工具与工件之间摩擦系数的模拟装置,测定了相同材质的带材在不同条件下的摩擦系数。
All friction coefficients between deformed press and die during sheet metal deep drawing were tested using new kinds of friction test device designed by authors.
在统计分析退火温度对冷轧IF钢深冲性能的影响的基础上,对不同退火温度下的断面金相组织亦进行了分析,并与进口料进行了对比。
The relationship of deep-drawing property and rolling parameters of IF steel was researched by the testing of ferritic rolling and annealing.
研究了深冲用3003-o铝合金带材合理的生产工艺,在化学成分和铸造、热轧、冷轧工艺确定的情况下,试验研究成品退火工艺制度。
Studied the annealing institution of 3003-o aluminum alloy strip for drawing is researched, while the chemical composition and casting, hot rolling, the cold rolling, process were determined.
研究了深冲用3003-o铝合金带材合理的生产工艺,在化学成分和铸造、热轧、冷轧工艺确定的情况下,试验研究成品退火工艺制度。
Studied the annealing institution of 3003-o aluminum alloy strip for drawing is researched, while the chemical composition and casting, hot rolling, the cold rolling, process were determined.