在感应淬火中,通过改变加热时间、加热功率和冷却速度可以改变淬硬层深度和硬度梯度。
The hardening case depth and hardness curve can be changed by adjusting heating time, heating power and cooling speed during induction hardening.
淬火层的深度是一个重要的工艺要求,它对产品的质量有很大影响。
Hardening layer depth is an important process requirements, it has great influence on the quality of products.
传统的曲轴淬火层深度测试方法是金相抽检,不能满足汽车工业生产需要。
Sampling examination by metallographic test was the traditional method for measuring the depth of the quenched layer in crankshaft, which could not meet the needs of the production of auto industry.
最后,采用新模型估算出激光淬火处理HT250材料硬化带深度的理论值,理论估算结果与试验结果吻合较好,且比简易激光相变硬化模型估算结果更接近于试验结果。
The new model has been used to evaluate the hardened depth of laser-quenched HT250, and the theoretical results are verified by the experiments and are more accurate than that of the old model.
论述了感应淬火零件的残余应力形态,并对载货车半轴的材料、硬化层深度及法兰圆角淬火层分布提出了个人见解。
This paper demonstrates residual stress of induction quench parts and personal views about stress distribution of flange corner heat treatment, truck half axle material and depth of hardened layer.
硬化层深度是等离子弧表面淬火效果的重要指标之一,而硬化层深度与工艺参数、淬火过程中温度场的变化密切相关。
Hardening depth related to the technical parameters and the quenching temperature field is an important target by plasma surface quenching.
基于锻后预冷淬火可提高工件的淬硬层深度,本文提出锻后余热预冷淬火工艺。
Based on that hardened case depth can be increased by delay in air after forging, the technique of delay quenching after forging is proposed in this paper.
利用A NSYS有限元分析软件,进行了6 110钢曲轴的中频感应淬火过程的模拟计算,并预测了淬硬层的深度,计算了淬火后的残余应力分布。
The simulation on medium frequency induction hardening process of crankshaft in 6110 engine is carried out by using FEA software ANSYS with hardening depth predicted and residual stress calculated.
摘要:对980钢进行激光相变硬化研究,分别对其空冷和水冷时淬火硬化层的宽度和深度进行测量,对其组织和硬化层硬度进行分析。
Abstract: The research of laser transformation hardening on steel 980 has been done in this paper. The width, depth and microhardness of quench zone was measured.
摘要:对980钢进行激光相变硬化研究,分别对其空冷和水冷时淬火硬化层的宽度和深度进行测量,对其组织和硬化层硬度进行分析。
Abstract: The research of laser transformation hardening on steel 980 has been done in this paper. The width, depth and microhardness of quench zone was measured.