在聚酯废料生产三角异形涤纶短纤维过程中存在影响纤维截面异形度的因素。
During producing triangular shaped polyester staple fiber from polyester waste, there are some factors that affect the heteroclite dacron fibres.
探讨了影响涤纶短纤维收缩率的工艺条件。
The technology conditions that have effect on polyester shrinkage rate were discussed.
根据油毛毡基布的生产工艺和技术指标确定涤纶短纤维的质量指标。
The quality index of PET staple fiber was defined according to production process and technical parameters of roofing felt.
阐述了涤纶短纤维油剂实验室可纺性评价体系的建立方法及其应用。
The establishment and application of experimental spinnability evaluation system were described for PET staple finish.
介绍了一种新的测试三维卷曲涤纶短纤维的膨松性能的方法——抽真空法。
A new testing method of vacuum-pumping for bulkiness property of three-dimensional crimp polyester staple fibers was introduced.
涤纶排管,涤纶短纤维,蓄电池配件,轻体材料,包装材料制品加工、造。
Dacron emission control Dacron short fibers, batteries accessories, light body materials, packaging materials products processing, manufacturing.
介绍了利用再生材料生产远红外三维卷曲中空涤纶短纤维的生产控制要点。
The focal points of control in the production of far infrared regenerated 3d crimp PET staple fiber was introduced.
通过异形喷丝板的设计及特殊纺丝和后拉伸工艺生产了闪光扁平涤纶短纤维。
Shine and flat polyester staple fiber was produced by using profiled spinneret and special spinning and drawing process.
在涤纶短纤维加工成形过程中对超、倍长纤维的严格控制是生产技术的关键。
The reasons of the formation of defects, split filament and double length fiber during the production of superfine PA staple fiber were analyzed.
涤纶短纤维无卷曲丝产品的生产,关键是在电气控制上实现联合机、曳引机的联动。
The key to the no crimping polyester staple fiber processing is to realize the unification of combined mechanism and tractive mechanism in electric control.
探讨了原丝预取向度、拉伸温度以及拉伸速度对涤纶短纤维强度变异系数的影响。
The effects of grey yarn pre-orientation degree, drawing temperature and drawing speed on the strength variable coefficient of polyester staple fiber are studied.
探讨了生产涤纶短纤维过程中产生超长、倍长纤维,卷曲率波动和比电阻升高的原因。
The reasons, which result in over length fiber, double length fiber, crimp ratio waving and specific resistance rising, were discussed.
采用非结晶聚酯切片制备高收缩涤纶短纤维,对切片干燥、纺丝、拉伸、定型等工艺进行了研究。
High shrinkage polyester staple was prepared by using amorphous polyester chip. The technology of drying, spinning, drawing and non-setting was studied.
采用了萃取称重法、萃取折射率法、快速法、核磁共振法测定了对涤纶短纤维的含油率进行了比较。
The finish oil content of PET staple fiber was determined by extraction weight method, extraction light refraction method, instant test method and nuclear magnetic resonance spectroscopy.
以某工程涤纶短纤维骤冷风空调系统为例,介绍了工业用组合式空调器的组成及其典型的控制方案。
Introducing a typical quench air system designed for a polymer spinning project, the features and control strategy of combination air-conditioner used at industrial area are given out.
与其他通用浆料比较,聚酯浆料对涤纶短纤维具有较好的粘附性,更适宜于对涤纶短纤维纱的上浆。
Comparing with common sizing agents, it has better adhesivity on polyester staple. It's more suitable for polyester staple yarn sizing. It is easy for desizing and it is more environmental protection.
文章介绍利用废弃聚酯生产棉型涤纶短纤维的可行性,生产设备工艺流程,工艺参数选择与效果分析。
The equipment, producing process, technical parameters and the result analysis were introduced. It showed that the preparation of cotton type polyester staple was feasible by using waste PET.
武城县大合成有限公司把废旧塑料经过几道复杂工序处理,加工成的涤纶短纤维可纺织成高档飞机地毯。
Da He Cheng limited company in Wucheng County can dispose the plastic wastes into Terylene fibers by several working procedures, and then weave to high grade airplane carpets.
涤纶短纤维与棉纤维混纺生产的产品,在穿着过程中会有起球问题,对于这类织物,烧毛工序更显得重要。
The use of polyester staple in blends with cotton, with the resultant pilling problem during wear, has increased the importance of singeing for these cloths.
应用FRS-XRSA、SAXS、DMA等研究了涤纶短纤维在纺丝及后处理过程中的结晶、取向与超结构的形成与变化。
The formation and the change of crystallinity, orientation and super structure of PET fiber during the spinning process were investigated by mean of FRS XRSA, SAXS and DMA.
针对纯细旦涤纶短纤纱和喷气织造工艺特点 ,合理制定了纯细旦涤纶短纤维经纱的上浆工艺 ,并取得了较好的织造效果。
The properties of fine denier polyester fiber and viscose fiber are introduced, and some factors affecting the yarn quality such as fiber properties and spinning process are analyzed.
本文对棉纺行业生产差别性涤纶短纤维仿毛织物的织造工艺和织物设计进行了研究,提出了仿毛织物的织造工艺和织物设计方法。
In this paper, the wool-like fabric designing and weaving process from modified polyester yarn in cotton mill were studied and put forward.
在聚酯废料生产三角异形涤纶短纤维过程中对影响纤维截面异形度的主要因素:喷丝孔截面形状、纺丝温度、冷却成形条件、后欠伸工艺参数等进行探讨。
During the process of spinning triangular heteroclite dacron fibres from polyester garbage, there are factors that may affect the hetercliteness of the intersecting surface of the fibres thus spun.
涤纶、锦纶短纤维制造、销售。
以负离子远红外聚丙烯母粒及聚丙烯切片为原料,在普通涤纶设备上共混纺丝制得负离子远红外丙纶短纤维。
Anionic far-infrared polypropylene staple fiber can be produced via blend spinning on a normal PET plant with anionic far-infrared polypropylene masterbatch and polypropylene chips as raw materials.
非对称冷却成形法是制造螺旋形三维卷曲涤纶中空短纤维的有效方法,冷却成形条件是纺丝过程的技术关键。
Unsymmertrical quenching is an effective method to prepare spiral three-dimension-crimp PET hollow fiber. Quench forming condition is the key technique in spinning.
用粘胶,涤纶,锦纶长丝,短纤维制造的各类化纤面料色彩缤纷,品种繁多。
Chemical fiber fabrics made from viscose, polyester and nylon filaments or staples have a great variety and a riot of color.
涤纶高收缩短纤维的制取,主要采用低温拉伸、适当降低拉伸倍率以及不定型工艺。
High shrinkage PET staple fiber is mainly made by the adoption of low temperature drawing, suitable reduction of draw ratio and non-setting process.
涤纶高收缩短纤维的制取,主要采用低温拉伸、适当降低拉伸倍率以及不定型工艺。
High shrinkage PET staple fiber is mainly made by the adoption of low temperature drawing, suitable reduction of draw ratio and non-setting process.