结果表明,当共聚单体N羟甲基丙烯酰胺(NMA)和甲基丙烯酸羟乙酯(HEMA)的质量分数分别为6%和15%时,树脂的交联度较高;
The results show that high cross-linking degree of resin can be gained as the mass fraction of comonomer N-hydroxymethyl acrylamide (NMA)and hydroxyethacrylate (HEMA)are 6% and 15% respectively.
讨论了环氧树脂的选择、混合方式、单体配比、树脂分子量和漆膜交联度等问题。
The selection of resins, mixing process, monomer ratio, molecular weight of the resin and film crosslinking density were discussed.
线性酚醛树脂是热交联型计算机直接制版版材的成膜树脂之一,它的性质对版材的灵敏度有很大影响。
Novolac was one of the resins forming the image films of computer to plate (CTP), and it's character directly determined the sensitivity of the CTP plate.
本文研究了低交联度季铵树脂的合成及其在酯类合成中的应用。
The synthesis of low cross-linking tertiary ammonium resin and its application to esters synthesis are studied in this paper.
以甲壳素为原料,采用正交试验法确定制备高脱乙酰度和高交联度的壳聚糖树脂的工艺条件。
For preparing chitosan resin of high deacetylation degree and high cross-linking degree, chitin is taken as raw material and orthogonal test is adopted to determine technological condition.
研究了加入高岭土的聚丙烯酸钠复合高吸水性树脂合成中反应温度、中和度、交联剂用量、引发剂用量、高岭土添加量等影响树脂吸水性能的主要因素。
The influence of reaction temperature, neutralization degree of acrylic acid and amounts of crosslinking agent, initiator, dispersant and kaolin on the absorbency of the composite was discussed.
以丙烯酸酯为单体,二乙烯基苯为交联剂,采用悬浮聚合法合成低交联度的聚丙烯酸酯类吸油树脂。
The acrylate oil absorbing resin were synthesised by means of suspension polymerization and using divinylbenzene as crosslinking agent.
本文还系统的考察了树脂在光固化时,两种基体树脂配比的不同、光引发剂用量的变化、光照时间的不同对于涂料固化交联度的影响。
The influence of the ratio of two resins, concentration of photoinitiator, and LTV' irradiation time on the properties of cured film was investigated also.
用互贯法合成了不同交联度的强碱弱酸两性树脂,考查了树脂交联度对两性树脂脱盐抗污染的影响。
The influence on desalination and anti-pollution by the different cross-linking degree of Amphoteric resins was investigated .
结果表明,改性的UF树脂固化后的交联度大于未改性树脂固化后的交联度。
The results showed the degree of the crosslinking of the modified UF resin was higher than that of the untreated UF resin.
这类聚合物的双叠氮交联剂组成的负型感光树脂具有高感度,高分辨率,稀碱水显影以及优良的抗蚀性能。
Some of the negative photopolymers composed of these polymers and bisazides can be developed in dilute aqueous base easily and clearly with excellent performance on photosensitivity and residual film.
本文较详细地介绍了表层低交联度聚苯乙烯树脂及接枝聚苯乙烯树脂的制备过程及它们的一些物理性质。
The preparation of thin layer polystyrene resin and grafted polystyrene resin as well as their physical properties have been described in detail.
本文较详细地介绍了表层代交联度聚苯乙烯树脂及接枝聚苯乙烯树脂的制备过程及它们的一些物理性质。
The preparation of thin layer polystyrene resin and grafted polystyrene resin aswell as their physical properties have been described in detail.
研究了引发剂用量、单体浓度、中和度、交联剂对树脂吸水倍率的影响。
The relationships between the absorption amount of super absorbent resin and initiator amount, monomer concentration, degree of neutralization, and…
研究了引发剂用量、单体浓度、中和度、交联剂对树脂吸水倍率的影响。
The relationships between the absorption amount of super absorbent resin and initiator amount, monomer concentration, degree of neutralization, and…