镀层中晶体取向具有轴向织构的特征。
确定了可能作为微波量子放大器的磁场数值和相应的晶体取向的工作点。
The magnitudes of the magnetic field and the corresponding crystal orientations at the possible operating points for maser operation have been thereby determined.
基于迹线分析法,开发了一种不需衍射花样的铸造合金晶体取向测算程序。
Based on the trace analysis, a computer program is developed to determine crystallographic orientations without using diffraction patterns.
计算结果表明:晶体取向和孔洞位置对试样蠕变损伤和裂纹萌生行为有着显著的影响。
The analysis results have shown that creep damage and crack initiation behaviour depend strongly on the void location and crystallographic orientation.
采用晶体取向分布函数(ODF)研究和分析了中间退火对高纯铝箔立方织构的影响。
The effect of middle annealing on cube texture of high-purity aluminum foils was investigated by means of orientation distribution functions (ODFs).
利用X射线衍射分析方法,对湿压磁场成型的永磁铁氧体生坯晶体取向度进行了研究。
Degree of preferred orientation of hard Sr ferrite compacts molded with magnetic field was studied by X ray diffraction analysis.
采用镍基合金粉,研究了激光多层涂覆过程中基材晶体取向对涂层凝固组织的影响规律。
The influence of the crystal orientation of the substrate on microstructure is investigated by multi layer laser cladding with the powder of nickel base superalloy.
采用晶体取向分布函数(ODF)、TEM研究了铁含量及退火对高纯铝箔再结晶织构的影响。
The influence of trace Fe and annealing on recrystallization texture of high purity aluminum foils was investigated by means of orientation distribution functions(ODFs)and TEM.
铜单晶线材中位错蚀坑密度与材料浸蚀时间,变形量以及晶体学取向有关。
The dislocation etch pits density(EPD) of copper single wires is related with corroded time, deformative extent and crystal orientation of material.
结果表明,聚合物对于控制晶体的取向生长起着关键性作用。
The results show that the polymer play a key role in controlling the orientation growth of crystals.
磁极间相互作用力很好地解释了晶体在强磁场下排列取向和聚集长大的现象。
Crystal alignment and assemblage phenomena in high magnetic field were caused by the reciprocity between magnetic poles.
采用速率敏感晶体塑性理论,预测了面心立方金属板材单轴拉伸过程中主要理想取向的稳定性。
Orientation stability during uniaxial tension of face-centered cubic (FCC) metal sheets is predicted using a rate-sensitive crystal plasticity model.
针对任意取向的双轴晶体,计算了完整的偏光干涉图,反映了相位分布决定等色线、振幅分布决定消光影的规律。
The conoscopic interference patterns of crystals are calculated for any orientation biaxial crystal, which include information of isochromatic curve and isogyre.
断裂韧性与晶体学取向的关系亦作了分析。
The relationship between fracture toughness and crystal orientation hasbeen also examined.
这种螺旋晶体就像一根具有一定取向的直晶棒被弯曲盘卷在一个圆柱面上,它不是自发地而是受人工控制形成的。
The spiral crystal is just like a straight crystal bar with definite orientation coiled on a cylindrical surface. It is not formed spontaneously, but is formed under control.
计算表明临界电流极强地依赖于两个晶体和结的相对取向,并在某些特殊的相对取向变为零。
The critical current depends strongly on the relative orientations among the two crystals and the junctions, vanishing in some special relative orientations.
与炭化处理纤维相比,石墨化纤维晶体结构更加完整,沿纤维主表面的取向程度更高。
In comparison with the carbonized fibers, the carbon fibers after graphitization treatment display more perfect crystal orientation along the main surface of ribbon-shaped carbon fibers.
非线性晶体adp的取向是使仅在两束光都存在时才有位相匹配的SHG。
The nonlinear ADP crystal is oriented in such a way that phase matched SHG is produced only when both incident beams are present as ordinary rays.
用阴影法和光学显微镜观察等方法揭示了BSO晶体中深色核芯与生长取向、界面形状及小面生长之间的关系。
The relationships among the darkened cores in the BSO crystals, growth direction, interface shape and growth of facets were revealed by methods of shadowgraph and microscopy.
由于外部晶场环境的改变,这两种体系的分子取向序与宏观C60晶体材料有着明显不同,并且出现了一些特殊现象。
Due to the change of the crystal field, their orientational orders are distinctly different from those in bulk system, and some unique phenomena appear.
利用高通滤波器进行滤波,观察到晶体的透射光的衍射效率与外加电压成线性关系,并与电场方向和晶体电正极面之相对取向有关,但是不依赖于入射光的偏振状态。
It was observed that the diffraction efficiency of the transmitted light shows a linear dependence on the applied voltage, but is independent of the polarization of the incident light.
图2 - 1 (a)给出了共发射极取向的晶体管的物理特性,同时也给出了硅器件的电压极性和大小。
Figure 2-1 (a) shows the physical representation of the BJT in its common-emitter orientation, and also shows typical voltage polarities and magnitudes for the case of a silicon device.
自组装有机膜能加速HAP晶体的形核速率,且有机膜功能团的种类及结构对HAP 晶体的形核与取向生长起决定作用。
The results show that, 1 the presence of organic films can accelerate the HAP crystal nucleation, but different organic film can induce HAP crystal with different growth style and crystal morphology.
自组装有机膜能加速HAP晶体的形核速率,且有机膜功能团的种类及结构对HAP 晶体的形核与取向生长起决定作用。
The results show that, 1 the presence of organic films can accelerate the HAP crystal nucleation, but different organic film can induce HAP crystal with different growth style and crystal morphology.