选取低硅无取向硅钢常化态板材，分别在不同速比下进行异步轧制，考察了速比对低硅无取向硅钢冷轧织构的影响。
The effect of speed ratio on the texture of non-oriented cold rolled low silicon steel sheet was investigated after cross shear rolling at different speed ratios.
结果表明，随着铸坯加热温度的提高，冷轧无取向硅钢成品晶粒尺寸减少，有利织构组分增加。
The results show that the grain size of cold-rolled non-oriented silicon steel finished product decreases and benefiting texture component increases with increasing slab reheating temperature.
对冷轧及退火后无取向硅钢织构及磁性能的变化进行研究。
The variation of the texture and magnetic properties of non-oriented silicon steel after being cold-rolled and annealed is studied.
研究了同步和异步轧制下无取向硅钢的冷轧织构及其沿层厚的分布特征。
This paper is to research the thickness distribution across the strip and it's relationship with roll's thermal crown in asymmetric rolling.
同全氢气氛相比较，氨分解气氛更有利于50aw 600无取向硅钢有利织构的形成。
Compared with pure hydrogen atmosphere, decomposed ammonia atmosphere is more propitious to the formation of advantaged texture of non-oriented silicon steel.
同全氢气氛相比较，氨分解气氛更有利于50aw 600无取向硅钢有利织构的形成。
Compared with pure hydrogen atmosphere, decomposed ammonia atmosphere is more propitious to the formation of advantaged texture of non-oriented silicon steel.