通过模拟试验,研究了泥浆的颗粒组成与泥浆的解胶曲线、高中压注浆成形速率及坯体挺形性等的关系。
By simulated test, the co-relationship among the slip granulometric composition, slurry deflocculation curve, mid-high pressure casting forming speed and green body shaping endurance is studied.
用压汞法测定了离心成形坯体的孔隙率,曲线呈窄的单峰分布,证明了粉体无团聚。
The results show that the distribution curves are one-humped and concentric, which indicates that the powders have no agglomeration.
用料浆喷涂法在Q235钢基体上成形覆层坯体;
The green body was formed by slurry spray method on the Q235 steel substrate.
随着炭黑含量的增加,成形坯体的线型收缩先减小后增大,坯体的强度则逐渐降低。
The linear shrinkage of green bodies showed an increase firstly but decreased with further increase in the carbon black content.
本发明是一种可通过对注射成形的多层预制坯(1)进行吹塑来获得的一体吹塑内装袋容器(2)。
The invention is an integrally blow-moulded bag-in-container (2) obtainable by blow-moulding an injection moulded multi-layer preform (1).
本发明是一种可通过对注射成形的多层预制坯(1)进行吹塑来获得的一体吹塑内装袋容器(2)。
The invention is an integrally blow-moulded bag-in-container (2) obtainable by blow-moulding an injection moulded multi-layer preform (1).