直接测定了铝电解质实际样品的初晶温度。
Liquidus temperature of actual aluminum electrolyte samples was measured directly.
并对磁场强度影响初晶硅迁移的机制进行了探讨。
The mechanism of influence of the magnetic flux density on the migratory behavior was discussed.
而使高硅铝合金充分发挥实用价值的关键是细化初晶硅。
The value of hypereutectic Al Si alloys is their fine primary silicon particles.
在初晶温度较低的电解质中,铝的溶解度较低,反之较高。
For electrolyte system with lower liquidus temperatures, the solubility of aluminium was lower too, vice versa.
当磁场强度达到6.6T时,初晶硅发生迁移并聚集,产生明显的聚集层;
The primary Si grains tend to migrate and form a remarkable Si-rich layer at magnetic flux of 6.6 T.
当磁场强度不变,随着磁场梯度的增大,初晶硅的偏聚量增加,晶粒尺寸变小。
The amount of segregated primary silicon grains increases with increasing magnetic gradient, whereas the grain size decreases.
随着变质温度的升高,稀土对初晶硅的变质作用加强,而对共晶硅的变质作用减弱。
With the increase of modifying temperature, the modification of rare earth Pr enhances on primary silicon, fades on eutectic silicon.
本品能优化与细化初晶硅及共晶硅形态及分布,变质具有长效性,重熔变质功效可遗传。
This product can optimize and fine the shape and distribution of primary crystal and eutectic silicon. The modification is long acting and remelting modification efficacy can pass down.
主要研究了初晶温度、过热度、电解质组成,以及电解质融化之后的熔盐深度对铝溶解度的影响。
Influence factors, such as liquidus temperature, superheat degree, electrolyte components, and the depth of molten salt were focused.
系统的输入参数除传统的电压、温度和分子比外,还采用初晶温度、过热度和阴极压降等作为系统的输入参数。
Besides the cell voltage, bath temperature and bath ratio, the inputs of the system also include the liquidus temperature, superheat extent and cathode voltage.
研究结果表明:1. P - RE复合变质对过共晶铝硅合金的初晶硅和共晶硅都具有良好的变质和细化作用。
The result indicated that: 1. P-RE combination modification can modify both the eutectic Si and primary Si of the hypereutectic Al-Si alloy at the same time.
在初晶相为鳞石英的平板玻璃中加入千分之几的P_2O_5后对析晶性能的影响与初晶相为硅灰石的平板玻璃是不同的。
The effect of addition of P_2O_5 in a few thousandths on the devitrification behavior of plate glass with primary phase of tridymite is different from that with primary phase of wollastonite.
通过调整氟化铝添加量、出铝量和设定电压,以及氧化铝下料间隔的自修正,实现对电解槽温度、初晶温度、效应系数的控制。
The bath temperature, liquidus and anode effect were controlled by adjusting the AlF3 additions, aluminum tapping magnitude, cell voltage set-point and the alumina feeding interval.
强磁场的磁化力和洛伦兹力通过控制初晶硅颗粒迁移行为来改变其在合金基体中的分布状态,通过影响凝固过程中的对流现象改变合金的凝固组织。
The results indicate that it is possible to control the behaviors of reinforced particles in the metal matrix by using intense magnetic fields in the solidification process of metal matrix composites.
三星在九月初投入使用的器兴研发生产基地承担起晶硅太阳能电池的生产任务。
Samsung's research and testing facility in Giheung houses its crystalline silicon solar cells first launched early in September.
到2011年初,晶艺浪漫婚典已经在全省超过13个市区提供过婚礼服务,并得到业内外各界人士的高度关注。
In the early 2011, Jingyi romantic wedding has provided romantic wedding services in more than 13 cities, and with high attention in this industry.
力学性能测试结果表明,除在临界二相区加热外,二次热循环均使粗晶区得到初化。
The results show that toughness of the coarse grained HAZ is improved after second welding heat cycle except intercritical two-phase heating.
力学性能测试结果表明,除在临界二相区加热外,二次热循环均使粗晶区得到初化。
The results show that toughness of the coarse grained HAZ is improved after second welding heat cycle except intercritical two-phase heating.