结果表明,弯折压平交替变形后,随热处理温度的升高,再结晶形核率增加。
The results show that after alternate deformation, with the increase of heat treatment temperature, the nucleation ratio of recrystallization rises.
进一步指出在预热处理中可以通过控制再结晶石墨的生长,来达到控制金刚石核量的目的。
It is put forward that, diamond nucleation amount can be controlled by controlling the growth of recrystallized graphite during the preheating period.
研究结果表明,双金属材料确定后,热处理芯轴尺寸和再结晶退火温度决定双金属环的最终尺寸。
The research result indicates that, when bimetal material is certain, the size of heat treatment mandrill and the temperature of re-crystallized anneal would decide the end size of bimetals wreaths.
然后执行热处理步骤,以便使有缺陷的半导体晶体材料的非晶化区域再结晶。
A thermal treatment step is next performed so as to recrystallize the amorphized region of the defective semiconductor crystal material.
叶片表面的再结晶在叶片使用之前就已存在,是由于固溶热处理前叶片的表面存在塑性变形,在固溶热处理过程中形成的。
Owing to the plastic deformation on the blade surface, recrystallization formed on the solid solution heat treatment. Before blade application, recrystallization zone existed already on its two sid…
叶片表面的再结晶在叶片使用之前就已存在,是由于固溶热处理前叶片的表面存在塑性变形,在固溶热处理过程中形成的。
Owing to the plastic deformation on the blade surface, recrystallization formed on the solid solution heat treatment. Before blade application, recrystallization zone existed already on its two sid…